SABIC Innovative Plastics LNP STAT-KON RD000IXP PA 66

Category Polymer , Thermoplastic , Nylon , Nylon 66
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP STAT-KON
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP STAT-KON RD000IXP PA 66.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP STAT-KON* RD000IXP is a compound based on Nylon 66 resin containing Carbon Powder. Added features of this material include: Electrically Conductive, High Impact.
Physical Properties Metric English Comments
Density 1.18 g/cc
0.0426 lb/in³
ISO 1183
1.19 g/cc
0.0430 lb/in³
ASTM D792
Moisture Absorption 0.630 %
0.630 %
50% RH, 24 hrs; ASTM D570
0.630 %
0.630 %
23°C / 50% RH; ISO 62
Linear Mold Shrinkage, Flow >= 0.020 cm/cm

@Time 86400 sec
 >= 0.020 in/in

@Time 24.0 hour
 ASTM D955
0.0292 cm/cm

@Time 86400 sec
 0.0292 in/in

@Time 24.0 hour
 ISO 294
Linear Mold Shrinkage, Transverse 0.020 - 0.040 cm/cm

@Time 86400 sec
 0.020 - 0.040 in/in

@Time 24.0 hour
 ASTM D955
0.0317 cm/cm

@Time 86400 sec
 0.0317 in/in

@Time 24.0 hour
 ISO 294
Mechanical Properties Metric English Comments
Tensile Strength at Break 50.0 MPa
7250 psi
5 mm/min; ISO 527
53.0 MPa
7690 psi
Type I, 5 mm/min; ASTM D638
Tensile Strength, Yield 51.0 MPa
7400 psi
5 mm/min; ISO 527
54.0 MPa
7830 psi
Type I, 5 mm/min; ASTM D638
Elongation at Break 12.2 %
12.2 %
Type I, 5 mm/min; ASTM D638
14.6 %
14.6 %
5 mm/min; ISO 527
Elongation at Yield 12 %
12 %
Type I, 5 mm/min; ASTM D638
14.3 %
14.3 %
5 mm/min; ISO 527
Tensile Modulus 2.23 GPa
323 ksi
1 mm/min; ISO 527
2.69 GPa
390 ksi
50 mm/min; ASTM D638
Flexural Strength 83.0 MPa
12000 psi
ISO 178
Flexural Modulus 2.49 GPa
361 ksi
1.3 mm/min, 50 mm span; ASTM D790
2.59 GPa
376 ksi
2 mm/min; ISO 178
Izod Impact, Notched 0.740 J/cm
1.39 ft-lb/in
ASTM D256
Izod Impact, Unnotched 10.6 J/cm
19.9 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 9.00 kJ/m²
4.28 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 111 kJ/m²
52.8 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 10.0 J

@Temperature 23.0 °C
 7.38 ft-lb

@Temperature 73.4 °F
 ASTM D3763
Impact Test 22.0 J
16.2 ft-lb
Multiaxial Impact; ISO 6603
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 88.7 µm/m-°C

@Temperature -30.0 - 30.0 °C
 49.3 µin/in-°F

@Temperature -22.0 - 86.0 °F
 ASTM D696
CTE, linear, Transverse to Flow 87.1 µm/m-°C

@Temperature -30.0 - 30.0 °C
 48.4 µin/in-°F

@Temperature -22.0 - 86.0 °F
 ASTM D696
Deflection Temperature at 0.46 MPa (66 psi) 190 °C
374 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
216 °C

@Thickness 3.20 mm
 421 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 65.0 °C
149 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
71.0 °C

@Thickness 3.20 mm
 160 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Electrical Properties Metric English Comments
Surface Resistance 2.0 - 6.0 ohm
2.0 - 6.0 ohm
ASTM D257