ExxonMobil Metallyte™ 18MM383 OPP Film

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Film Grade
Manufacturer Exxon Chemical
Trade Name Metallyte™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil Metallyte™ 18MM383 OPP Film.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: A biaxially oriented very high barrier metalized polypropylene film. This film offers an outstanding moisture barrier and a broad seal range surface on the other side. This film is designed for high performance packaging applications.Availability: Africa & Middle East, Asia Pacific and EuropeKey Features:Excellent adhesion of aluminum to filmExcellent moisture barrierExcellent light barrierVery good hot tackBroad seal rangeHigh yieldBrilliant metal appearanceFeatures: Broad Seal RangeGrease ResistantLight BarrierMoisture BarrierApplications:Biscuits/Cookie/CrackersConfectionery, Chocolate Confectionery, Gum Confectionery, Sugar Crisps and Snacks Uses: VFFS Flexible Packaging Processing Method: Inner Web Adhesive LaminationInformation provided by ExxonMobil
Physical Properties Metric English Comments
Water Vapor Transmission 0.202 g/m²/day

@Temperature 38.0 °C
0.0130 g/100 in²/day

@Temperature 100 °F
90% RH; ExxonMobil Method
Thickness 18.0 microns
0.710 mil
ExxonMobil Method
Coating Weight 16.2 g/m²
10.1 lb/ream
ExxonMobil Method
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 175 %
175 %
7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
Film Elongation at Break, TD 60 %
60 %
7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
Modulus of Elasticity 2.00 GPa
290 ksi
MD; ExxonMobil Method
3.60 GPa
522 ksi
TD; ExxonMobil Method
Coefficient of Friction 0.40
0.40
Unmetallized Size (Broad Seal Range Surface); ExxonMobil Method
Seal Strength 460 g/25 mm

@Pressure 0.276 MPa,
Temperature 140 °C
460 g/in

@Pressure 40.0 psi,
Temperature 284 °F
Otto Brugger, 0.2 sec; ExxonMobil Method
Film Tensile Strength at Break, MD 150 MPa
21800 psi
7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
Film Tensile Strength at Break, TD 290 MPa
42100 psi
7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
Thermal Properties Metric English Comments
Shrinkage, MD 6.5 %

@Temperature 135 °C,
Time 432 sec
6.5 %

@Temperature 275 °F,
Time 0.120 hour
ExxonMobil Method
Shrinkage, TD 4.5 %

@Temperature 135 °C,
Time 432 sec
4.5 %

@Temperature 275 °F,
Time 0.120 hour
ExxonMobil Method
Optical Properties Metric English Comments
Optical Density 2.7
2.7
ExxonMobil Method
Descriptive Properties Value Comments
Heat Seal Range 72°F
36.3 psi, 0.2 sec
Yield 43000 in2/lb