SABIC Innovative Plastics LNP LUBRICOMP RL004 PA 66

Category Polymer , Thermoplastic , Nylon , Nylon 66
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP LUBRICOMP RL004 PA 66.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* LUBRICOMP* RL004 is a copmpound based on Nylon 66 resin containing 20% PTFE. Added feature of this grade includes: Wear Resistant.
Physical Properties Metric English Comments
Density 1.25 g/cc
0.0452 lb/in³
ISO 1183
1.25 g/cc
0.0452 lb/in³
ASTM D792
Moisture Absorption 0.790 %
0.790 %
50% RH, 24 hrs; ASTM D570
1.20 %
1.20 %
23°C / 50% RH; ISO 62
Linear Mold Shrinkage, Flow >= 0.020 cm/cm

@Time 86400 sec
>= 0.020 in/in

@Time 24.0 hour
ASTM D955
Linear Mold Shrinkage, Transverse 0.010 - 0.030 cm/cm

@Time 86400 sec
0.010 - 0.030 in/in

@Time 24.0 hour
ASTM D955
Mechanical Properties Metric English Comments
Hardness, Rockwell M 56
56
ASTM D785
Hardness, Rockwell R 110
110
ASTM D785
Tensile Strength at Break 69.0 MPa
10000 psi
5 mm/min; ISO 527
71.0 MPa
10300 psi
Type I, 5 mm/min; ASTM D638
Tensile Strength, Yield 69.0 MPa
10000 psi
5 mm/min; ISO 527
71.0 MPa
10300 psi
Type I, 5 mm/min; ASTM D638
Elongation at Break 6.7 %
6.7 %
Type I, 5 mm/min; ASTM D638
7.9 %
7.9 %
5 mm/min; ISO 527
Elongation at Yield 6.3 %
6.3 %
Type I, 5 mm/min; ASTM D638
7.7 %
7.7 %
5 mm/min; ISO 527
Tensile Modulus 3.05 GPa
442 ksi
1 mm/min; ISO 527
3.20 GPa
464 ksi
50 mm/min; ASTM D638
Flexural Strength 90.0 MPa
13100 psi
ISO 178
Flexural Modulus 2.68 GPa
389 ksi
1.3 mm/min, 50 mm span; ASTM D790
2.72 GPa
395 ksi
2 mm/min; ISO 178
Izod Impact, Notched 0.350 J/cm
0.656 ft-lb/in
ASTM D256
Izod Impact, Unnotched 5.97 J/cm
11.2 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 3.00 kJ/m²
1.43 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 36.0 kJ/m²
17.1 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 4.00 J

@Temperature 23.0 °C
2.95 ft-lb

@Temperature 73.4 °F
ASTM D3763
Impact Test 1.00 J
0.738 ft-lb
Multiaxial Impact; ISO 6603
Coefficient of Friction, Dynamic 0.32
0.32
ASTM D3702 Modified
Coefficient of Friction, Static 0.21
0.21
ASTM D3702 Modified
K (wear) Factor 32.2 x 10-8 mm³/N-M
16.0 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D3702 Modified
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 90.0 µm/m-°C

@Temperature -30.0 - 30.0 °C
50.0 µin/in-°F

@Temperature -22.0 - 86.0 °F
ASTM D696
CTE, linear, Transverse to Flow 88.0 µm/m-°C

@Temperature -30.0 - 30.0 °C
48.9 µin/in-°F

@Temperature -22.0 - 86.0 °F
ASTM D696
Deflection Temperature at 0.46 MPa (66 psi) 201 °C
394 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
239 °C

@Thickness 3.20 mm
462 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 68.0 °C
154 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
71.0 °C

@Thickness 3.20 mm
160 °F

@Thickness 0.126 in
unannealed; ASTM D648