SABIC Innovative Plastics Cycolac® INP576 ABS

Category Polymer , Thermoplastic , ABS Polymer
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Cycolac®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Cycolac® INP576 ABS.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Can be used as compounding additives for polymer blends. Medium molecular weight SAN. Can be blended with high rubber graft modifier resins to produce customized ABS properties. Suitable for direct weather exposure. Most versatile SAN for balance of processing and physical properties.This data was supplied by SABIC-IP for the Americas region.
Physical Properties Metric English Comments
Specific Gravity 1.08 g/cc
1.08 g/cc
ASTM D 792
Density 1.08 g/cc
0.0390 lb/in³
ISO 1183
Melt Flow 23 g/10 min

@Load 3.80 kg,
Temperature 230 °C
23 g/10 min

@Load 8.38 lb,
Temperature 446 °F
ASTM D 1238
78 g/10 min

@Load 10.0 kg,
Temperature 220 °C
78 g/10 min

@Load 22.0 lb,
Temperature 428 °F
ISO 1133
Mechanical Properties Metric English Comments
Hardness, Rockwell R 122
122
ASTM D 785
Tensile Strength at Break 68.0 MPa
9860 psi
Type I, 5 mm/min; ASTM D 638
Tensile Strength, Yield 41.0 MPa
5950 psi
Type I, 5 mm/min; ASTM D 638
Elongation at Break 2.2 %
2.2 %
Type I, 5 mm/min; ASTM D 638
Elongation at Yield 1.4 %
1.4 %
Type I, 5 mm/min; ASTM D 638
Tensile Modulus 3.97 GPa
576 ksi
5 mm/min; ASTM D 638
Flexural Yield Strength 68.0 MPa
9860 psi
2 mm/min; ISO 178
96.0 MPa
13900 psi
1.3 mm/min, 50 mm span; ASTM D 790
Flexural Modulus 3.54 GPa
513 ksi
2 mm/min; ISO 178
3.57 GPa
518 ksi
1.3 mm/min, 50 mm span; ASTM D 790
Izod Impact, Notched 0.130 J/cm

@Temperature -30.0 °C
0.244 ft-lb/in

@Temperature -22.0 °F
ASTM D 256
0.210 J/cm

@Temperature 23.0 °C
0.393 ft-lb/in

@Temperature 73.4 °F
ASTM D 256
Izod Impact, Notched (ISO) 1.00 kJ/m²

@Temperature 23.0 °C
0.476 ft-lb/in²

@Temperature 73.4 °F
80*10*4; ISO 180/1A
1.00 kJ/m²

@Temperature -30.0 °C
0.476 ft-lb/in²

@Temperature -22.0 °F
80*10*4; ISO 180/1A
Charpy Impact Unnotched 0.100 J/cm²

@Temperature 23.0 °C
0.476 ft-lb/in²

@Temperature 73.4 °F
ISO 179/2C
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 98.0 °C

@Thickness 3.20 mm
208 °F

@Thickness 0.126 in
unannealed; ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 84.0 °C
183 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
87.0 °C

@Thickness 3.20 mm
189 °F

@Thickness 0.126 in
unannealed; ASTM D 648
Vicat Softening Point 102 °C
216 °F
Rate B/50; ISO 306
106 °C
223 °F
Rate B/120; ISO 306
Optical Properties Metric English Comments
Yellow Index 1.0 %
1.0 %
ASTM D 1925