SABIC Innovative Plastics LNP LUBRICOMP DL004 PC

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP LUBRICOMP DL004 PC.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Lubricomp* DL004 is a compound based on Polycarbonate resin containing 20% PTFE. Added features of this material include: Internally Lubricated.
Physical Properties Metric English Comments
Specific Gravity 1.30 g/cc
1.30 g/cc
ASTM D792
Density 1.30 g/cc
0.0470 lb/in³
ASTM D792
1.30 g/cc
0.0470 lb/in³
ISO 1183
Moisture Absorption 0.250 %
0.250 %
50% RH, 24 hrs; ASTM D570
0.360 %
0.360 %
23°C / 50% RH; ISO 62
Linear Mold Shrinkage, Flow 0.0059 cm/cm

@Time 86400 sec
0.0059 in/in

@Time 24.0 hour
ISO 294
0.0050 - 0.0070 cm/cm

@Time 86400 sec
0.0050 - 0.0070 in/in

@Time 24.0 hour
ASTM D955
Linear Mold Shrinkage, Transverse 0.0064 cm/cm

@Time 86400 sec
0.0064 in/in

@Time 24.0 hour
ISO 294
0.0060 - 0.0080 cm/cm

@Time 86400 sec
0.0060 - 0.0080 in/in

@Time 24.0 hour
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 39.0 MPa
5660 psi
Type I, 5 mm/min; ASTM D638
39.0 MPa
5660 psi
5 mm/min; ISO 527
Tensile Strength, Yield 43.0 MPa
6240 psi
Type I, 5 mm/min; ASTM D638
44.0 MPa
6380 psi
5 mm/min; ISO 527
Elongation at Break 28.9 %
28.9 %
Type I, 5 mm/min; ASTM D638
29.3 %
29.3 %
5 mm/min; ISO 527
Elongation at Yield 5.9 %
5.9 %
5 mm/min; ISO 527
6.2 %
6.2 %
Type I, 5 mm/min; ASTM D638
Tensile Modulus 2.05 GPa
297 ksi
1 mm/min; ISO 527
2.08 GPa
302 ksi
50 mm/min; ASTM D638
Flexural Strength 63.0 MPa
9140 psi
ISO 178
73.0 MPa
10600 psi
ASTM D790
Flexural Modulus 1.93 GPa
280 ksi
2 mm/min; ISO 178
2.06 GPa
299 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 1.07 J/cm
2.00 ft-lb/in
ASTM D256
Izod Impact, Unnotched 18.7 J/cm
35.0 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 11.0 kJ/m²
5.23 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 178 kJ/m²
84.7 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 24.0 J
17.7 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
24.0 J

@Temperature 23.0 °C
17.7 ft-lb

@Temperature 73.4 °F
ASTM D3763
Impact Test 21.0 J
15.5 ft-lb
Multiaxial Impact; ISO 6603
Coefficient of Friction, Dynamic 0.25
0.25
ASTM D3702 Modified
Coefficient of Friction, Static 0.21
0.21
ASTM D3702 Modified
K (wear) Factor 14.1 x 10-8 mm³/N-M
7.00 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D3702 Modified
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 77.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
42.8 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
77.4 µm/m-°C

@Temperature -40.0 - 40.0 °C
43.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
CTE, linear, Transverse to Flow 75.6 µm/m-°C

@Temperature -40.0 - 40.0 °C
42.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
76.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
42.2 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 143 °C
289 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
141 °C

@Thickness 3.20 mm
286 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 129 °C
264 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
128 °C

@Thickness 3.20 mm
262 °F

@Thickness 0.126 in
unannealed; ASTM D648