SABIC Innovative Plastics LNP LUBRICOMP DL002PC PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP DL002PC PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* LUBRICOMP* DL002PC is a compound based on Polycarbonate resin containing 10% PTFE. Added features of this grade are: Wear Resistant, Exceptional Processing, Clean Compound System.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.24 g/cc | 0.0448 lb/in³ | ASTM D792 |
| 1.25 g/cc | 0.0452 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.100 % | 0.100 % | 50% RH, 24 hrs; ASTM D570 |
| 0.200 % | 0.200 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0070 - 0.0090 cm/cm @Time 86400 sec |
0.0070 - 0.0090 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0070 - 0.0090 cm/cm @Time 86400 sec |
0.0070 - 0.0090 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.012 cm/cm @Time 86400 sec |
0.010 - 0.012 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 43.0 MPa | 6240 psi | 5 mm/min; ISO 527 |
| 44.0 MPa | 6380 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 53.0 MPa | 7690 psi | Type I, 5 mm/min; ASTM D638 |
| 54.0 MPa | 7830 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 23.1 % | 23.1 % | 5 mm/min; ISO 527 |
| 30.5 % | 30.5 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 5.3 % | 5.3 % | Type I, 5 mm/min; ASTM D638 |
| 5.6 % | 5.6 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 2.45 GPa | 355 ksi | 50 mm/min; ASTM D638 |
| 2.46 GPa | 357 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 82.0 MPa | 11900 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 85.0 MPa | 12300 psi | ISO 178 | |
| Flexural Modulus | 2.07 GPa | 300 ksi | 2 mm/min; ISO 178 |
| 2.20 GPa | 319 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 1.06 J/cm | 1.99 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | NB | NB | ASTM D4812 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² | 4.76 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | NB | NB | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 34.0 J | 25.1 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 74.0 J | 54.6 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.28 | 0.28 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.17 | 0.17 | ASTM D3702 Modified |
| K (wear) Factor | 195 x 10-8 mm³/N-M | 97.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 66.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
36.7 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 67.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
37.2 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 72.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
40.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 73.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
40.6 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 123 °C | 253 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 120 °C @Thickness 3.20 mm |
248 °F @Thickness 0.126 in |
unannealed; ASTM D648 |