SABIC Innovative Plastics LNP LUBRICOMP DFL23 PC (Asia Pacific)

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP LUBRICOMP DFL23 PC (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Lubricomp* DFL23 is a compound based on Polycarbonate resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated.
Physical Properties Metric English Comments
Density 1.38 g/cc
0.0499 lb/in³
ASTM D792
1.38 g/cc
0.0499 lb/in³
ISO 1183
Moisture Absorption 0.100 %
0.100 %
50% RH, 24 hrs; ASTM D570
Linear Mold Shrinkage, Flow 0.0038 cm/cm

@Time 86400 sec
0.0038 in/in

@Time 24.0 hour
ISO 294
0.0030 - 0.0050 cm/cm

@Time 86400 sec
0.0030 - 0.0050 in/in

@Time 24.0 hour
ASTM D955
Linear Mold Shrinkage, Transverse 0.0050 - 0.0070 cm/cm

@Time 86400 sec
0.0050 - 0.0070 in/in

@Time 24.0 hour
ASTM D955
0.0060 cm/cm

@Time 86400 sec
0.0060 in/in

@Time 24.0 hour
ISO 294
Mechanical Properties Metric English Comments
Tensile Strength at Break 67.0 MPa
9720 psi
ASTM D638
88.0 MPa
12800 psi
ISO 527
Tensile Strength, Yield 88.0 MPa
12800 psi
ASTM D638
88.0 MPa
12800 psi
ISO 527
Elongation at Break 3.0 %
3.0 %
ISO 527
3.5 %
3.5 %
ASTM D638
Elongation at Yield 2.9 %
2.9 %
ISO 527
3.1 %
3.1 %
ASTM D638
Tensile Modulus 5.33 GPa
773 ksi
1 mm/min; ISO 527
5.51 GPa
799 ksi
50 mm/min; ASTM D638
Flexural Strength 137 MPa
19900 psi
ASTM D790
142 MPa
20600 psi
ISO 178
Flexural Modulus 4.82 GPa
699 ksi
ASTM D790
5.10 GPa
740 ksi
ISO 178
Izod Impact, Notched 1.54 J/cm
2.89 ft-lb/in
ASTM D256
Izod Impact, Unnotched 7.58 J/cm
14.2 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 13.0 kJ/m²
6.19 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 44.0 kJ/m²
20.9 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 23.0 J
17.0 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Impact Test 7.00 J
5.16 ft-lb
Multiaxial Impact; ISO 6603
Coefficient of Friction, Dynamic 0.49
0.49
ASTM D3702 Modified
Coefficient of Friction, Static 0.54
0.54
ASTM D3702 Modified
K (wear) Factor 326 x 10-8 mm³/N-M
162 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D3702 Modified
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 46.8 µm/m-°C

@Temperature -40.0 - 40.0 °C
26.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
47.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
26.1 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 43.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
23.9 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
43.2 µm/m-°C

@Temperature -40.0 - 40.0 °C
24.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
Deflection Temperature at 0.46 MPa (66 psi) 145 °C
293 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
145 °C

@Thickness 3.20 mm
293 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 141 °C
286 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
140 °C

@Thickness 3.20 mm
284 °F

@Thickness 0.126 in
unannealed; ASTM D648