Polymer Property : Tensile Strength at Break = 12800 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	88.3 MPa	12800 psi	Type I, 5.1 mm/min; ASTM D638
PolyOne Nymax™ 604 NU Natural Polyamide 6 Alloy (Nylon 6 Alloy) The Nymax® 600 Blend Series of nylon 6 materials are salt-and-pepper pelletized blends combining select nylon resins and process aids, performance modifiers, and color concentrates. These materials..
Tensile Strength at Break	88.3 MPa	12800 psi	ASTM D638
Parker Chomerics PREMIER™ A230-ST EMI Shielding Plastic Description: PREMIER™ is the world’s first and most versatile commercially available conductive thermoplastic for real world EMI shielding solutions. It is a blend of PC/ABS thermoplastic polymer ..
Tensile Strength at Break	88.0 MPa	12800 psi	ASTM D638
SABIC Innovative Plastics LNP KONDUIT PTF2BXXX PA 6 LNP KONDUIT* PTF2BXXX is a compound based on Nylon 6 resin containing 10% Glass Fiber, 55% Proprietary Thermal Filler. Added features of this material include: Thermally Conductive.
Tensile Strength at Break	88.0 MPa	12800 psi	ISO 527
SABIC Innovative Plastics LNP LUBRICOMP DFL23 PC (Asia Pacific) LNP* Lubricomp* DFL23 is a compound based on Polycarbonate resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated.
Tensile Strength at Break	88.3 MPa	12800 psi	ASTM D638
Ravago Manufacturing Americas Enviramid™ N1315HL BK Post Consumer Recycle Nylon 66, 15% Glass Filled Heat Stabilized, Lubricated, Black, and made from EnViramid™ Post Consumer Recycled NylonInformation provided by Ravago.
Tensile Strength at Break	88.0 MPa	12800 psi	ISO 527
SABIC Innovative Plastics LNP LUBRICOMP DFL23 PC LNP* Lubricomp* DFL23 is a compound based on Polycarbonate resin containing 15% Glass Fiber and 10% PTFE. Added features include: Internally Lubricated.
Tensile Strength at Break	88.0 MPa	12800 psi	5mm/min; ISO 527-2/1A
Celanese ZENITE ZE55201 LCP, 50% Mineral / Glass Reinforced (Unverified Data**) Zenite® ZE55201 is a 50% mineral/glass fiber reinforced liquid crystal polymer for injection molding. and It is specifically suitable for applications requiring ultra flatness.50% glass/mineral rei..
Tensile Strength at Break	88.0 MPa	12800 psi	50mm/min; ISO 527-2/1A
Celanese FORTRON 1200L1 PPS, Specialty (Unverified Data**) Fortron 1200L1 is an unfilled grade for extrusion applications, which has a high melt viscosity and tensile elongation. The recommended processing conditions are identical to those of our standard ..
Tensile Strength at Break	88.0 MPa	12800 psi	ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP GFL36L PSU (Asia Pacific) LNP* Lubricomp* GFL36L is a compound based on Polysulfone resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated, Low Extractible.
Tensile Strength at Break	88.0 MPa	12800 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP KFL36 Acetal Copolymer (Asia Pacific) LNP* Lubricomp* KFL36 is a compound based on Acetal Copolymer resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated.
Tensile Strength at Break	88.0 MPa	12800 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP THERMOCOMP 2X98703 ETFE LNP* THERMOCOMP* 2X98703 is a compound based on ETFE Copolymer resin containint Proprietary Filler(s).
Tensile Strength at Break	88.0 MPa	12800 psi	ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP ZF0049 PPE+PS (Asia Pacific) LNP* Thermocomp* ZF0049 is a compound based on PPE+PS Blend resin containing Flame Retardant. Added features of this material include: Flame Retardant.
Tensile Strength at Break	88.0 MPa	12800 psi	ASTM D638
Sumitomo Bakelite North America E 8354A-1 Short Glass Fiber Reinforced Epoxy E 8354A-1 is a fiberglass and mineral reinforced epoxy molding compound, with excellent dimensional stability, good electrical insulation properties, and good strength.Information provided by Sumito..
Tensile Strength at Break	88.0 MPa	12800 psi	Nominal Stress, brk, Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics NORYL GTX GTX810 PPE+PS+PA 10% Glass Reinforced PPE+PA Alloy.
Tensile Strength at Break	88.0 MPa	12800 psi	5 mm/min; ISO 527
SABIC Innovative Plastics ULTEM AUT210 PEI Transparent, Thermoplastic Polyimide (TPI). Glass transition Temperature (Tg) of 227degC. Haze onset temperature of 212degC (SABIC IP method). Very low outgassing and plateout, for automotive lighti..
Tensile Strength at Break	88.0 MPa	12800 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics ULTEM AUT210 PEI (Asia Pacific) Transparent Polyetherimide (Tg 227 degC). Very low outgassing and plateout, for automotive lighting applications where highly metallized, reflective surfaces are required. Haze onset temperature o..
Tensile Strength at Break	88.0 MPa	12800 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics ULTEM AUT210 PEI (Europe-Africa-Middle East) Transparent Polyetherimide (Tg 227 degC). Very low outgassing and plateout, for automotive lighting applications where highly metallized, reflective surfaces are required. Haze onset temperature o..
Tensile Strength at Break	88.0 MPa	12800 psi	5 mm/min; ISO 527
SABIC Innovative Plastics ULTEM AUT210 PEI (Europe-Africa-Middle East) Transparent Polyetherimide (Tg 227 degC). Very low outgassing and plateout, for automotive lighting applications where highly metallized, reflective surfaces are required. Haze onset temperature o..
Tensile Strength at Break	88.0 MPa	12800 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics NORYL GTX GTX4610 PPE+PA (Asia Pacific) Noryl GTX* GTX4610 resin is a high performance, 10% glass filled blend of PPE/PA that exhibits an excellent balance of non-halogenated flame retardance, dimensional stability, high heat resistance, ..
Tensile Strength at Break	88.0 MPa	12800 psi	5 mm/min; ISO 527
SABIC Innovative Plastics NORYL GTX GTX4610 PPE+PA (Asia Pacific) Noryl GTX* GTX4610 resin is a high performance, 10% glass filled blend of PPE/PA that exhibits an excellent balance of non-halogenated flame retardance, dimensional stability, high heat resistance, ..
Tensile Strength at Break	88.0 MPa	12800 psi	5 mm/min; ISO 527
SABIC Innovative Plastics NORYL GTX GTX4610 PPE+PA (Europe-Africa-Middle East) Noryl GTX* GTX4610 resin is a high performance, 10% glass filled blend of PPE/PA that exhibits an excellent balance of non-halogenated flame retardance, dimensional stability, high heat resistance, ..
Tensile Strength at Break	88.0 MPa	12800 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics NORYL GTX GTX810 PPE+PS+PA (Asia Pacific) GR 10%. Increased stiffness of 200000 psi (3000 MPa) flexural modulus. Excellent chemical and high heat resistance. Application: lighting.
Tensile Strength at Break	88.0 MPa	12800 psi	ISO 527-2
Tisan TISLAMID® 66 30% Mineral Reinforced Nylon 66 TISLAMID has a wide area of application in electric/electronic, automotive, durable goods and telecommunications industries. It demonstrates characteristics such as Excellent chemical resistanceElec..
Tensile Strength at Break	88.0 MPa	12800 psi	ISO 527-93
Wellman Wellamid® MRGF1475 BK01 20% Mineral/Glass Reinforced Nylon 66 Description: Mineral/Glass Reinforced Nylon 66Information provided by Wellman.
Tensile Strength at Break	88.3 MPa	12800 psi	ASTM D 638
RTP Company RTP 2599 X 131264 A Polycarbonate/ABS Alloy (PC/ABS), Fiber Reinforced - Electrically Conductive - EMI/RFI Shielding
Tensile Strength at Break	88.0 MPa	12800 psi	5 mm/min; ISO 527
Eurostar Starflam A28UL PA66, Flame Retardant, Injection Molding Staramide A28UL is Unfilled, Halogen Free and Red Phosphorous Free, Flame Retardant Polyamide 66, Injection Molding ResinInformation provided by Eurostar.
Tensile Strength at Break	88.0 MPa	12800 psi	5mm/min; ISO 527-2/1A
Celanese Celanex® XFR 6842 GF20 PBT, 30% Glass Reinforced Celanex XFR 6842 GF20 is a halogen and antimony free flame retardant (V-0 @ 0.4 mm) 20% glass reinforced PBT grade with good processability and no corrosive emissions during processing. It is suita..
Tensile Strength at Break	88.0 MPa	12800 psi	5mm/min; ISO 527-2/1A
Celanese Celstran® PP-GF20-23AF3001 Natural PP, 20% Glass Reinforced Celstran PP-Gf20-23 is a 20% long glass fiber Polypropylene. The -23 can be used in food contact applications since all of the raw materials contained within are FDA compiant. This material imparts ..
Tensile Strength at Break	88.0 MPa	12800 psi	ASTM D638
Beijing Chemical Industry KAIFA® 301-G15 PBT Resin 15% glass fiber reinforced, flame retardantInformation provided by Beijing Chemical Industry Research Institute (Group)
Tensile Strength at Break	88.0 MPa	12800 psi	5mm/min; ISO 527-2/1A
Celanese ZENITE ZE55201 LCP, 50% Mineral / Glass Reinforced Zenite« ZE55201 is a 50% mineral/glass fiber reinforced liquid crystal polymer for injection molding. and It is specifically suitable for applications requiring ultra flatness.Information provided ..