Polymer Property : Flexural Strength = 142 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Strength	142 MPa	20600 psi	ISO 178
SABIC Innovative Plastics LNP LUBRICOMP DFL23 PC (Asia Pacific) LNP* Lubricomp* DFL23 is a compound based on Polycarbonate resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated.
Flexural Strength	142 MPa	20600 psi	ISO 178
SABIC Innovative Plastics LNP LUBRICOMP DCP32 PC LNP* Lubricomp* DCP32 is a compound based on Polycarbonate resin containing 15% PTFE/Silicone, 10% Carbon Fiber. Added features of this material include: Electrically Conductive, Internally Lubrica..
Flexural Strength	142 MPa	20600 psi	ISO 178
SABIC Innovative Plastics LNP LUBRICOMP DFL23 PC LNP* Lubricomp* DFL23 is a compound based on Polycarbonate resin containing 15% Glass Fiber and 10% PTFE. Added features include: Internally Lubricated.
Flexural Strength	142 MPa	20600 psi	ASTM D790
LG Chemical EH910 PMMA, General Purpose Grade for Extrusion Excellent solvent resistanceHighest of all grades in heat resistance, mechanical strength, surface hardness and stress cracking resistanceFeatures: Excellent transparency and eleganceWeather resista..
Flexural Strength	142 MPa	20600 psi	ASTM D790
Kolon KOCETALÂ® GF302 G/F Reinforced Acetal Resin Glass fiber reinforced, improved stiffness. Applications: Products for high stiffness, improved fatigue properties.Information provided by API-Kolon.
Flexural Strength	142 MPa	20600 psi	ASTM D790
Kotec Carbotex KG-30F15 Polycarbonate, Wear Resistant, 30% Glass Fiber Reinforced Features: Glass fiber 30% reinforced, Mold release, Translucent, Dimensional stability, Non-frictionApplications: OA equipment, Communications, Precision parts, Machineries, E & E partsInformation p..
Flexural Strength	142 MPa @Temperature 22.0 Â°C	20600 psi @Temperature 71.6 Â°F	25 mm wide 100 mm long, flat samples; ISO 14125
Menzolit MenzolitÂ® SMC 0200 Unsaturated Polyester UP SMC 0200 is a general purpose SMC for a wide range of applications. Typically, it is used as housings, covers and functional components in mechanical engineering. The flammability meets the demands ..
Flexural Strength	142 MPa	20600 psi	ASTM D790
SABIC Innovative Plastics LNP STAT-KON DX04403 PC LNP STAT-KON* DX04403 is a compound based on Polycarbonate resin containing Proprietary Filler(s). Added features of this material include: Electrically Conductive, Flame Retardant.
Flexural Strength	142 MPa	20600 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP STAT-KON DX04403 PC LNP STAT-KON* DX04403 is a compound based on Polycarbonate resin containing Proprietary Filler(s). Added features of this material include: Electrically Conductive, Flame Retardant.
Flexural Strength	142 MPa	20600 psi	ISO 178
SABIC Innovative Plastics LNP THERMOCOMP WX05502 Polyester Elastomer LNP THERMOCOMP* WX05502 is a compound based on Polyester, TP resin containing Flame Retardant, Glass Fiber, Mineral. Added features of this material include: Flame Retardant.
Flexural Strength	142 MPa	20600 psi	1.3 mm/min, 50 mm span; ASTM D 790
SABIC Innovative Plastics LNP Verton NV0061EV_GY7E148 PC+ABS Preliminary data for 30% long fiber single pellet non-halogen FR color filled PC/ABSThis data was supplied by SABIC-IP for the Americas region.
Flexural Strength	142 MPa	20600 psi	ASTM D790
SABIC Innovative Plastics NORYL GFN2L PPE+PS (Asia Pacific) PPE+PS GF20%, hydrolytic stability
Flexural Strength	142 MPa	20600 psi	at rupture; ASTM D790
Sumitomo Bakelite North America E 2748A Short Glass Fiber Reinforced Epoxy E 2748A is a glass reinforced epoxy molding compound, with good impact strength combined with soft flow for the encapsulation of devices requiring high quality and thermal shock resistance.Informati..
Flexural Strength	142 MPa	20600 psi
Toyobo ECOVYLOPET® EMC2310 PET Bottle Recycling Grade, 10% Glass Reinforced Features: PET Bottle Recycling Grade, 10% Glass Fiber Reinforced, General PurposeApplications: Automobile engine head coversHot platesVending machine partsUmbrella ribsInformation provided by Toyobo..
Flexural Strength	142 MPa	20600 psi	ASTM D790
Beijing Ranger Chem PBT-201-G10 272 Flame Retarding FR PBT Modified PBT Characteristics: Unreinforced grades have abundant strength and flexibility, and have strong characteristics against brittleness. UL-certified slow-burning (94HB) and self-extinguishin..
Flexural Strength	142 MPa	20600 psi	ASTM D790
A. Schulman ComAlloy Hiloy® 412 Polyester - PBT, Glass Reinforced Data provided by the manufacturer, ComAlloy International Company.15% Glass Reinforced.The ComAlloy product line has been integrated into the A Schulman product line.
Flexural Strength	142 MPa	20600 psi	ASTM D790
A. Schulman ComAlloy Hiloy® 631 Nylon 6/6, Glass Reinforced, Flow Enhanced Data provided by the manufacturer, ComAlloy International Company.15% Glass Reinforced.The ComAlloy product line has been integrated into the A Schulman product line.
Flexural Strength	142 MPa	20600 psi	ASTM D790
Gromax CCP PBT 4815-NCB 15% Glass Fiber Filled Product Description: A glass fiber 15% reinforced injection molding grade. Characteristics:Excellent electrical property Excellent temperature resistance, high heat distortion temperature Excellent ..
Flexural Strength	142 MPa	20600 psi	ISO 178
SABIC Innovative Plastics LNP LUBRICOMP DCP32 PC (Asia Pacific) LNP* Lubricomp* DCP32 is a compound based on Polycarbonate resin containing PTFE, Carbon Fiber, Silicone. Added features of this material include: Electrically Conductive, Internally Lubricated.
Flexural Strength	142 MPa	20600 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP STAT-KON OE002 PPS - LINEAR LNP* STAT-KON* OE002 is a compound based on PPS - Linear resin containing 10% Carbon Fiber. Added feature of this material is: Electrically Conductive.
Flexural Strength	142 MPa	20600 psi	ASTM D790
SABIC Innovative Plastics NORYL PX2944 PPE+HIPS (Asia Pacific) PPE/PS, GF20%, high heat, non-FR