SABIC Innovative Plastics LNP LUBRICOMP DBL349E PC

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP LUBRICOMP DBL349E PC.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Lubricomp* DBL349E is a compound based on Polycarbonate resin containing 20% Glass Bead, 15% PTFE, Flame Retardant. Added features of this material include: Internally Lubricated, Flame Retardant.
Physical Properties Metric English Comments
Density 1.48 g/cc
0.0535 lb/in³
ASTM D792
1.48 g/cc
0.0535 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.0040 - 0.0060 cm/cm

@Time 86400 sec
0.0040 - 0.0060 in/in

@Time 24.0 hour
ASTM D955
0.0054 cm/cm

@Time 86400 sec
0.0054 in/in

@Time 24.0 hour
ISO 294
Linear Mold Shrinkage, Transverse 0.0069 cm/cm

@Time 86400 sec
0.0069 in/in

@Time 24.0 hour
ISO 294
0.0060 - 0.0080 cm/cm

@Time 86400 sec
0.0060 - 0.0080 in/in

@Time 24.0 hour
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 37.0 MPa
5370 psi
ASTM D638
38.0 MPa
5510 psi
ISO 527
Tensile Strength, Yield 41.0 MPa
5950 psi
ASTM D638
41.0 MPa
5950 psi
ISO 527
Elongation at Break 7.6 %
7.6 %
ISO 527
9.0 %
9.0 %
ASTM D638
Elongation at Yield 2.8 %
2.8 %
ISO 527
2.9 %
2.9 %
ASTM D638
Tensile Modulus 2.97 GPa
431 ksi
1 mm/min; ISO 527
3.44 GPa
499 ksi
50 mm/min; ASTM D638
Flexural Strength 78.0 MPa
11300 psi
ISO 178
Flexural Modulus 2.75 GPa
399 ksi
ASTM D790
2.90 GPa
421 ksi
ISO 178
Izod Impact, Notched 0.580 J/cm
1.09 ft-lb/in
ASTM D256
Izod Impact, Unnotched 4.64 J/cm
8.69 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 5.00 kJ/m²
2.38 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 30.0 kJ/m²
14.3 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 15.0 J
11.1 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Impact Test 4.00 J
2.95 ft-lb
Multiaxial Impact; ISO 6603
Coefficient of Friction, Dynamic 0.51
0.51
ASTM D3702 Modified
Coefficient of Friction, Static 0.70
0.70
ASTM D3702 Modified
K (wear) Factor 181 x 10-8 mm³/N-M
90.0 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D3702 Modified
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 64.8 µm/m-°C

@Temperature -40.0 - 40.0 °C
36.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
65.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
36.1 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 64.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
35.6 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
64.8 µm/m-°C

@Temperature -40.0 - 40.0 °C
36.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
Deflection Temperature at 0.46 MPa (66 psi) 140 °C
284 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
141 °C

@Thickness 3.20 mm
286 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 129 °C
264 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
128 °C

@Thickness 3.20 mm
262 °F

@Thickness 0.126 in
unannealed; ASTM D648