Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Strength | 78.0 MPa | 11300 psi | ISO 178 |
Nilit FRIANYL B63 AL40 Nylon 6.6 for injection molding, 40% aluminum filled Nylon 6.6 for injection molding.Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
Flexural Strength | <= 78.0 MPa | <= 11300 psi | ISO 178 |
Polykemi AB POLYshine PBT D211 PBT, Modified Information provided by Polykemi AB |
|||
Flexural Strength | <= 78.0 MPa | <= 11300 psi | ISO 178 |
Polykemi AB POLYabs F20 ABS Information provided by Polykemi AB |
|||
Flexural Strength | <= 78.0 MPa | <= 11300 psi | ISO 178 |
Polykemi AB POLYabs F20 UV4 ABS, UV-stabilized Information provided by Polykemi AB |
|||
Flexural Strength | 78.0 MPa | 11300 psi | ASTM D790 |
LG Chemical LUCEL FW-7005 Friction and Wear Resistant POM, Oil filled LUCEL semi-crystalline acetal copolymer resins are produced by gas phase polymerization. LUCEL resins can be widely accepted as the replacement of thermosets, aluminum and zinc die-casts or other m.. |
|||
Flexural Strength | 78.0 MPa | 11300 psi | ASTM D790 |
LG Chemical LUCEL FW-715C Friction and Wear Resistant POM, Polymeric Wear Additive, CaCo3 Filled, Low Warpage, Antistatic LUCEL semi-crystalline acetal copolymer resins are produced by gas phase polymerization. LUCEL resins can be widely accepted as the replacement of thermosets, aluminum and zinc die-casts or other m.. |
|||
Flexural Strength | 78.0 MPa | 11300 psi | ASTM D790 |
Kolon KOCETAL® K300BK Black Colored Grade Acetal Resin Colored, general purpose injection molding grade. Applications: General injection molding products.Information provided by API-Kolon. |
|||
Flexural Strength | 78.0 MPa | 11300 psi | ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP RL0049S PA 66 LNP LUBRICOMP* RL0049S is a compound based on Nylon 66 resin containing 20% PTFE. Added features of this material include: Flame Retardant, Heat Stabilized, Wear Resistant. |
|||
Flexural Strength | 78.0 MPa | 11300 psi | ISO 178 |
SABIC Innovative Plastics LNP LUBRILOY D2000 PC (Asia Pacific) LNP LUBRILOY* D2000 is a compound based on Polycarbonate resin containing Proprietary Lubricant. Added features of this material include: Internally Lubricated. |
|||
Flexural Strength | 78.0 MPa | 11300 psi | ISO 178 |
SABIC Innovative Plastics LNP Lubriloy D2000XXH PC LNP LUBRILOY* D2000XXH is a compound based on Polycarbonate resin containing Proprietary Lubricant. Added features of this material include: Internally Lubricated, Healthcare.This data was supplied.. |
|||
Flexural Strength | 78.0 MPa | 11300 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Valox® 357 PBT+PC PC/PBT, Unreinforced, impact modified, UL94V-0 rated. Applications like bobbins, switches and enclosures. |
|||
Flexural Strength | 78.0 MPa | 11300 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics XYLEX HX8300HP PC+POLYESTER (Asia Pacific) Medium flow, Transparent PC/Polyester alloy. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP Class VI), food contact compliant... |
|||
Flexural Strength | 78.0 MPa | 11300 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics XYLEX X8300 PC+POLYESTER PC+Polyester, UV Stabilized, Transparent |
|||
Flexural Strength | 78.0 MPa | 11300 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Xylex X8300HP PC+POLYESTER (Asia Pacific) Transparent, US Food Contact compliant, chemically resistant.
This grade will no longer be supported with biocompatibility information and should not be used for medical applications which require b.. |
|||
Flexural Strength | 78.0 MPa | 11300 psi | ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP 67001XXH PBT+PC LNP* THERMOCOMP* 67001XXH is a compound based on PC + PBT resin containing proprietary antimicrobial additives. Designed for touch surfaces in patient critical healthcare applications. Added featu.. |
|||
Flexural Strength | 78.0 MPa | 11300 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
SABIC Innovative Plastics LNP Thermocomp WB006 PBT LNP* Thermocomp* WB006 is a compound based on Polybutylene Terephalate resin containing Glass Bead.This data was supplied by SABIC-IP for the Americas region. |
|||
Flexural Strength | 78.0 MPa | 11300 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP NX11302 PC+ABS (Asia Pacific) This is a PC/ABS compound with colorable, good plating, surface and mechanical performance, a good candidate for Laser Direct Structuring applications |
|||
Flexural Strength | 78.0 MPa | 11300 psi | ASTM D790 |
SABIC Innovative Plastics NORYL N1052P PPE+HIPS (Asia Pacific) PPE+PS 105deg.C FR V-2 |
|||
Flexural Strength | 78.0 MPa | 11300 psi | ISO 178 |
SABIC Innovative Plastics NORYL PX0844 PPE+PS PPE+PS blend. Unfilled. UL94 HB rated. Low water absorption. Hydrolytic stability. Dimensional stability. |
|||
Flexural Strength | 78.0 MPa | 11300 psi | ASTM D790 |
SABIC Innovative Plastics NORYL PX2801Z PPE+HIPS (Asia Pacific) PPE+HIPS Unfilled FR V-0 100C |
|||
Flexural Strength | 78.0 MPa | 11300 psi | ASTM D790 |
Plenco 4485 Phenolic, Granular, Compression Molded PLENCO 04485 is a mineral filled phenolic molding compound offering excellent heat resistance, electrical resistance, and dimensional stability. UL recognized under component file E40654. 04485 is a.. |
|||
Flexural Strength | 78.0 MPa | 11300 psi | ASTM D790 |
Unitika M1030E PA6, Conditioned Nano composite nylonInformation provided by Unitika Ltd. |
|||
Flexural Strength | 78.0 MPa | 11300 psi | ISO 178 |
Denka MALECCA K-200 ABS A heat-resistant ABS resin based on "DENKA IP" – a Styrene-N-Phenylmaleimide copolymer. It has been designed as an easy-to-use resin by improving conventional heat-resistant ABS resins which had de.. |
|||
Flexural Strength | 78.0 MPa | 11300 psi | ASTM D790 |
Beijing Chemical Industry KAIFA® M105 MPPO Resin Flame retardant, Thermal resistantInformation provided by Beijing Chemical Industry Research Institute (Group) |
|||
Flexural Strength | 78.0 MPa | 11300 psi | GB/9341 |
Zhejiang Juner PC/PBT Alloy Applications: Shell of Small Household Electric Appliance, Auto Electric Appliance PartsInformation provided by Zhejiang Juner New Materials Co, Ltd. |
|||
Flexural Strength | 78.0 MPa | 11300 psi | ASTM D790 |
Plenco 7307 Phenolic, Granular, Transfer Molded PLENCO 07307 is an organic fiber reinforced phenolic molding compound, offering improved mechanical strength properties. Type ASTM 5948 CFG, and UL recognized under component file E40654. 07307 is a.. |
|||
Flexural Strength | 78.0 MPa | 11300 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics XYLEX X8300CL PC+POLYESTER (Europe-Africa-Middle East) PC+Polyester, UV Stabilized, Transparent, OQ Quality |
|||
Flexural Strength | 78.0 MPa | 11300 psi | ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP DBL349E PC LNP* Lubricomp* DBL349E is a compound based on Polycarbonate resin containing 20% Glass Bead, 15% PTFE, Flame Retardant. Added features of this material include: Internally Lubricated, Flame Retard.. |
|||
Flexural Strength | 78.0 MPa | 11300 psi | ASTM D 790 |
SABIC Innovative Plastics LNP Lubricomp GZL34E PSU LNP LUBRICOMP* GZL34E is a compound based on Polysulfone resin containing Glass Fiber, Milled Glass, PTFE. Added features of this material include: Easy Molding.This data was supplied by SABIC-IP f.. |