SABIC Innovative Plastics LNP Konduit MT00EL PP
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP Konduit |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Konduit MT00EL PP.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Konduit* MT00EL is a Polypropylene base resin with thermal fillers. Characteristics of this grade are Thermal Conductivity and it is Low Extraactible.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.94 g/cc | 1.94 g/cc | ASTM D 792 |
| Density | 1.94 g/cc | 0.0701 lb/in³ | ASTM D 792 |
| Moisture Absorption at Equilibrium | 0.030 % | 0.030 % | 23°C / 50% RH; ISO 62 |
| 0.30 % @Time 86400 sec |
0.30 % @Time 24.0 hour |
50% RH; ASTM D 570 | |
| Linear Mold Shrinkage, Flow | 0.010 - 0.030 cm/cm @Time 86400 sec |
0.010 - 0.030 in/in @Time 24.0 hour |
ASTM D 955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.030 cm/cm @Time 86400 sec |
0.010 - 0.030 in/in @Time 24.0 hour |
ASTM D 955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 13.0 MPa | 1890 psi | 5 mm/min; ISO 527 |
| 14.0 MPa | 2030 psi | Type I, 5 mm/min; ASTM D 638 | |
| Tensile Strength, Yield | 14.0 MPa | 2030 psi | 5 mm/min; ISO 527 |
| 15.0 MPa | 2180 psi | Type I, 5 mm/min; ASTM D 638 | |
| Elongation at Break | 3.6 % | 3.6 % | 5 mm/min; ISO 527 |
| 4.8 % | 4.8 % | Type I, 5 mm/min; ASTM D 638 | |
| Elongation at Yield | 2.0 % | 2.0 % | Type I, 5 mm/min; ASTM D 638 |
| 2.0 % | 2.0 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 1.84 GPa | 267 ksi | 1 mm/min; ISO 527 |
| 7.21 GPa | 1050 ksi | 50 mm/min; ASTM D 638 | |
| Flexural Strength | 28.0 MPa | 4060 psi | ISO 178 |
| Flexural Yield Strength | 29.0 MPa | 4210 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Flexural Modulus | 4.54 GPa | 658 ksi | 2 mm/min; ISO 178 |
| 4.78 GPa | 693 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Izod Impact, Notched | 0.170 J/cm @Temperature 23.0 °C |
0.318 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 1.43 J/cm @Temperature 23.0 °C |
2.68 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 2.00 kJ/m² @Temperature 23.0 °C |
0.952 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 10.0 kJ/m² @Temperature 23.0 °C |
4.76 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| 9.00 J @Temperature 23.0 °C |
6.64 ft-lb @Temperature 73.4 °F |
Instrumented Impact Total Energy; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 53.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
29.4 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D 696 |
| CTE, linear, Transverse to Flow | 53.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
29.4 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D 696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 112 °C | 234 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 111 °C @Thickness 3.20 mm |
232 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 66.0 °C | 151 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 66.0 °C @Thickness 3.20 mm |
151 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |