Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 13.0 MPa | 1890 psi | 500 mm/min; ASTM D638 - ISO 527-2 |
DuPont Elvaloy® 1214 AC Ethylene and 14% Methyl Acrylate Copolymer
(discontinued **) Elvaloy® 1214 AC is intended for film coextrusion and injection molding. It can be recommended in film applications where softness, flexibility and excellent sealing properties are needed.Elvaloy®.. |
|||
Tensile Strength at Break | 13.0 MPa | 1890 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics NORYL WCP781 PPE-TPE Flexible PPE-TPE injection grade. Low specific gravity with very good halogen free flame retardant performance. Suitable for over-molding applications such as plugs, strain relief's, and connecto.. |
|||
Tensile Strength at Break | 13.0 MPa | 1890 psi | ASTM D638 |
SABIC Innovative Plastics LNP STAT-KON FX98500C PE (Asia Pacific) LNP* Stat-kon* FX98500C is a compound based on Polyethylene resin containing Carbon Powder. Added features of this material include: Electrically Conductive. |
|||
Tensile Strength at Break | 13.0 MPa | 1890 psi | ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP TH0450C PU LNP* Thermocomp* TH0450C is a compound based on Polyurethane resin containing High Specific Gravity Filler. Added features of this material include: High Specific Gravity. |
|||
Tensile Strength at Break | 13.0 MPa | 1890 psi | ASTM D638 |
ELASTO UK Dryflex® 660850S SEBS Based Material, Semi-Filled Qualities, 85A Hardness, Natural The 660-series is recommended when the properties of the produced detail requires the advantages of the 500-series in combination with the 600-series. A semi-filled material can therefore combine t.. |
|||
Tensile Strength at Break | 13.0 MPa | 1890 psi | ISO 527-2 |
ExxonMobil Exxtral™ BMU 139 Performance Polyolefin Product Description: A specialty thermoplastic polyolefin resin characterized by a good stiffness/toughness balance for automotive exterior applications such as bumper fascia.Availability: Asia Paci.. |
|||
Tensile Strength at Break | 13.0 MPa | 1890 psi | ISO 527-2/50 |
ExxonMobil Exxtral™ BNT 010 Performance Polyolefin Product Description: A specialty thermoplastic polyolefin resin designed for automotive exterior painted parts such as bumper fascia.Availability: Africa & Middle East, Asia Pacific, Europe, South A.. |
|||
Tensile Strength at Break | >= 13.0 MPa | >= 1890 psi | ISO R 527 |
Fainplast Compounds CKL 009 Flexible PVC, Sheathing Lead Free General purposes |
|||
Tensile Strength at Break | >= 13.0 MPa | >= 1890 psi | ISO R 527 |
Fainplast Compounds CL 73/1 Flexible PVC, Sheathing General purposes |
|||
Tensile Strength at Break | >= 13.0 MPa | >= 1890 psi | ISO R 527 |
Fainplast Compounds CL 75/1 Flexible PVC, Sheathing General purposes |
|||
Tensile Strength at Break | >= 13.0 MPa | >= 1890 psi | ISO R 527 |
Fainplast Compounds CL 82 Flexible PVC, Sheathing General purposes |
|||
Tensile Strength at Break | >= 13.0 MPa | >= 1890 psi | ISO R 527 |
Fainplast Compounds GK 75 Flexible PVC, Flame Retardant Sheathing Lead Free General purposes |
|||
Tensile Strength at Break | >= 13.0 MPa | >= 1890 psi | ISO R 527 |
Fainplast Compounds CL 76/2 Flexible PVC, Sheathing General purposes |
|||
Tensile Strength at Break | >= 13.0 MPa | >= 1890 psi | ISO R 527 |
Fainplast Compounds GA 76/R Flexible PVC, Flame Retardant Sheathing Mineral Oil resistent |
|||
Tensile Strength at Break | >= 13.0 MPa | >= 1890 psi | ISO R 527 |
Fainplast Compounds HG 82 Flexible PVC, Sheathing for High Temperatures Sheathing general purposes |
|||
Tensile Strength at Break | 13.0 MPa | 1890 psi | ISO R 527 |
Fainplast Compounds MPH 67 Medical Flexible PVC, Extrusion Tubolar apparatus |
|||
Tensile Strength at Break | 13.0 MPa | 1890 psi | ISO R 527 |
Fainplast Compounds PG 56/B Flexible PVC, Extrusion Modified with Rubber Hydrocarbon resisting tubes |
|||
Tensile Strength at Break | 13.0 MPa | 1890 psi | ISO R 527 |
Fainplast Compounds PH 66/A Flexible PVC, Transparent Extrusion Profiles, UL Class V2 |
|||
Tensile Strength at Break | 13.0 MPa | 1890 psi | ASTM D638 |
Aclo Accucomp Polypropylene CPO407L Copolymer |
|||
Tensile Strength at Break | 13.0 MPa | 1890 psi | ASTM D638 |
Aclo Accutech Polypropylene Copolymer CP0437M20L Mica Reinforced |
|||
Tensile Strength at Break | 13.0 MPa | 1890 psi | ASTM D638 |
Aclo Accutech Polypropylene Copolymer CP0437T30L Talc Reinforced |
|||
Tensile Strength at Break | 13.0 MPa | 1890 psi | ASTM D638 |
Aclo Accutech Polypropylene Homopolymer HP0339C20L1 Calcium Reinforced |
|||
Tensile Strength at Break | >= 13.0 MPa | >= 1890 psi | ASTM D4745-97 |
Adamas Adalon® 406 PTFE, 15% PEEK Information provided by Adamas, HPM |
|||
Tensile Strength at Break | 13.0 MPa | 1890 psi | ISO R 527 |
Fainplast Compounds PH 62 Flexible PVC, Transparent Extrusion Transparent profiles |
|||
Tensile Strength at Break | >= 13.0 MPa | >= 1880 psi | ASTM D412 Method A |
Seals Eastern 7045 Ethylene-Propylene Rubber General service EPDM.Information provided by Seals Eastern, Inc. |
|||
Tensile Strength at Break | 13.0 MPa | 1890 psi | ISO R 527 |
Fainplast Compounds PM 8050 Flexible PVC, Lead Free Pipes and profiles |