Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 14.0 MPa | 2030 psi | ISO 527-1/-2 |
Murtfeldt Murflor® + Bronze Polytetrafluoroethylene, 60% Bronze The addition of 60% bronze to the base material reduces the expansion coefficient and gives lower sliding wear.Special Properties:• Lower sliding wear than Murflor®• Good slide properties• Low s.. |
|||
Tensile Strength, Yield | 14.0 MPa | 2030 psi | Type IV, 510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Wire & Cable Y594B Polyvinyl Chloride, Flexible (PVC, Flexible) Typical Properties of Molded Slab (0.075); Not to be Construed as Specifications.Information provided by PolyOne |
|||
Tensile Strength, Yield | 14.0 MPa | 2030 psi | ASTM D412 |
Polymax® Maxelast® A9955H TPE, ABS/PC Overmold Polymax's TPE material complies with UL, VDE, FDA, RoHS and PAH's standards.Uses:Consumer ProductsToys & NoveltiesAuto PartsTool Hand GripsSporting GoodsWire & Cable ElectronicsMedical DevicesInform.. |
|||
Tensile Strength, Yield | 14.0 - 17.0 MPa | 2030 - 2470 psi | 50 mm/min; ISO/R 527 |
Okulen® 1000 PE-UHMW, Green Black OKULEN® 1000 is an ultra high molecular low pressure polyethylene with a molecular weight of < 3.5 g/mol. It has great wear resistance, high impact strength, and excellent sliding properties ideal .. |
|||
Tensile Strength, Yield | 14.0 MPa | 2030 psi | ASTM D412 |
Precision Polymer Engineering N60K Nitrile Rubber Peroxide Cured, Nitrile Butadiene Rubber (NBR), 55-65 °IRHD. Copolymer of acrylonitrile and butadiene. Formulated using only those ingredients determined by the United States Food and Drug Admini.. |
|||
Tensile Strength, Yield | 14.0 MPa | 2030 psi | ASTM D412 |
Precision Polymer Engineering Q70W Polyurethane Rubber Peroxide cured, off-white Polyurethane Rubber, 65-75 °IRHD. Polyester-based urethane. To meet ASTM line call-out M5BG714, B14, EO14, EO34. ASTM & ISO designation = AU.Applications: Excellent abra.. |
|||
Tensile Strength, Yield | 14.0 MPa | 2030 psi | ASTM D412 |
Precision Polymer Engineering V75F Fluoroelastomer Compound Special steam resistant, Fluoroelastomer Rubber, 70-80 °IRHD. Tetrapolymer of vinylidene fluoride, hexafluoropropylene and tetrafluoroethylene and cure site monomer (CSM). To meet ASTM D2000 line.. |
|||
Tensile Strength, Yield | 14.0 MPa | 2030 psi | ASTM D412 |
Precision Polymer Engineering V80B Fluoroelastomer Compound Fluoroelastomer Rubber, 76-85 °IRHD. Copolymer of vinylidene fluoride and hexafluoropropylene. To meet ASTM D2000 line call-out: M2HK814, A1-10, B37, B38, EF31, EO78, F15, Z1. Where Z1 = compressi.. |
|||
Tensile Strength, Yield | 14.0 MPa | 2030 psi | ASTM D412 |
Precision Polymer Engineering V80H Fluoroelastomer Compound Fluoroelastomer Rubber, 75-85 °IRHD. Copolymer of vinylidene fluoride and hexafluoropropylene. Formulated using only those ingredients determined by the United States Federal Food and Drug Adminis.. |
|||
Tensile Strength, Yield | 14.0 MPa | 2030 psi | ASTM D412 |
Precision Polymer Engineering V90M Fluoroelastomer Compound Brown Fluoroelastomer Rubber, 85-95 °IRHD. Copolymer of vinylidene fluoride and hexafluoropropylene. To meet ASTM D2000 line call-out: M3HK914, A1-10, B38, EF31, EO78, Z1, Z2, where Z1 = Brown and.. |
|||
Tensile Strength, Yield | 14.0 MPa | 2030 psi | ASTM D412 |
Precision Polymer Engineering Z60B Hydrogenated NBR Compound Hydrogenated Nitrile Rubber, 55-65 °IRHD. Medium acrylonitrile (ACN) content. ASTM designation = HNBR. ASTM D2000 line call-out 2MDH614, A26, B36, EO16, EO36, F14.Applications: High strength and .. |
|||
Tensile Strength, Yield | 14.0 MPa | 2030 psi | ASTM D638 |
Petroquimica Triunfo Trithene® TS 9022 MDPE - Overwrap Packaging The Trithene TS 9022 resin is a medium-density polyethylene (MDPE) with good optical properties, excellent stiffness and processability, that warrants the production of thin films with good appearan.. |
|||
Tensile Strength, Yield | 14.0 MPa | 2030 psi | 500 mm/min (20 in./min.); ASTM D638, Type IV Specimen |
Eastman 1924P Polyethylene
(discontinued **) Low-density polyethylene 1924P is a resin in the boardstock coating industry for use in breadboard, cupstock, and liquid packaging board. This material has an excellent combination of low neck-in, .. |
|||
Tensile Strength, Yield | 14.0 MPa | 2030 psi | ASTM D638 |
Petroquimica Triunfo Trithene® CX 8087 MDPE - Cast Film The Trithene CX 8087 resin is a medium density polyethylene (MDPE) with medium molecular weight that presents excellent balance between mechanical properties, processability and stiffness, allowing .. |
|||
Tensile Strength, Yield | 14.0 - 20.0 MPa | 2030 - 2900 psi | Average value: 16.6 MPa Grade Count:5 |
Overview of materials for Polytetrafluoroethylene (PTFE), Bronze Filled This property data is a summary of similar materials in the MatWeb database for the category "Polytetrafluoroethylene (PTFE), Bronze Filled". Each property range of values reported is minimum and ma.. |
|||
Tensile Strength, Yield | >= 14.0 MPa | >= 2030 psi | |
Kazanorgsintez 298-285D High Density Polyethylene Composite Production Method: Compositions are achieved by ethylene copolymerization by gaseous-phase method at low pressure using complex catalysts on carrier material. Application: HDPE compositions 296-.. |
|||
Tensile Strength, Yield | 14.0 MPa @Strain 0.200 %, Temperature 1204 °C |
2030 psi @Strain 0.200 %, Temperature 2199 °F |
|
Haynes HR-160® alloy, solution annealed sheet Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
Tensile Strength, Yield | 14.0 MPa | 2030 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP 2X00858 FP-F (FEP) LNP* THERMOCOMP* 2X00858 is a compound based on FEP resin containing proprietary fillers. |
|||
Tensile Strength, Yield | 14.0 MPa | 2030 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP Thermocomp MH0255A PP (Europe-Africa-Middle East) LNP* THERMOCOMP* MH0255A is a compound based on Polypropylene resin containing Proprietary Filler(s). Added features include; High Specific Gravity.This data was supplied by SABIC-IP for the Europe-.. |
|||
Tensile Strength, Yield | 14.0 MPa | 2030 psi | 50 mm/min; ISO 527-2 |
Borealis Bormed™ LE6609-PH LDPE for Pharmaceutical Blow Molding Bormed LE6609-PH is a LD-polyethylene produced in a high-pressure process intended for blow molding of soft and flexible packages for pharmaceutical products.Bormed LE6609-PH can be used in "blow-fi.. |
|||
Tensile Strength, Yield | 14.0 MPa | 2030 psi | ASTM D638 |
Eastman Eastman AP006 Copolyester Applications:Automotive componentsBreathable filmsElectrical/electronic componentsFilm ModificationFlexible hingesHose mandrelIndustrial componentsIndustrial hoses/beltsOffice furniturePackagingPoly.. |
|||
Tensile Strength, Yield | 14.0 MPa @Strain 300 % |
2030 psi @Strain 300 % |
ISO 527-1/-2 |
Covestro Desmopan® DP 8785A S043 Polyurethane injection molding gradewith special UV stabilizersexcellent abrasion resistanceEasy releaseshort cycle timesApplicationSports shoe solesPreprocessingMax. Water content |
|||
Tensile Strength, Yield | 14.0 MPa | 2030 psi | 50 mm/min; ISO 527 |
Eurostar Starflam MX05075 PP, Flame Retardant, Injection Molding Starflam MX05075 is an Unfilled Halogen Free Flame Retardant PP Injection Molding ResinInformation provided by Eurostar. |
|||
Tensile Strength, Yield | 14.0 MPa | 2030 psi | ISO 527 |
Azoty Tarnow™ TARFLEN SM-G15 PTFE Tarflen SM1 reinforced with 15% graphite for standard compression molding.Information provided by Zakłady Azotowe w Tarnowie-Moscicach S.A. |
|||
Tensile Strength, Yield | 14.0 MPa | 2030 psi | ISO 527 |
Azoty Tarnow™ TARFLEN SM-K25 PTFE Based on Tarflen SM1 reinforced with 25% coke for standard compression molding.Information provided by Zakłady Azotowe w Tarnowie-Moscicach S.A. |
|||
Tensile Strength, Yield | 14.0 MPa | 2030 psi | ISO 527 |
Breplast Bretene PP Polypropylene Composite Recovered polypropylene compositeInformation provided by Breplast S.p.A. |
|||
Tensile Strength, Yield | 14.0 MPa @Temperature 120 °C |
2030 psi @Temperature 248 °F |
ASTM Test |
BASF Ultramid® 8350 HS PA6 (Dry) Ultramid 8350 HS is a heat stabilized, impact modified type 6 graft copolymer developed for extrusion, tubing, and jacketing applications requiring a high level of toughness combined with a moderate.. |
|||
Tensile Strength, Yield | 14.0 MPa | 2030 psi | ASTM D638 |
Huntsman PE1076 Film Extrusion Polyethylene
(discontinued **) Homopolymer and FDA compliant.Features: Yields film with high clarity and excellent stiffness.Applications: Film extrusion: overwrap packaging.FDA Notes: Conforms to FDA regulation 21 CFR 177.1520 (.. |
|||
Tensile Strength, Yield | 14.0 - 55.0 MPa | 2030 - 7980 psi | Average value: 26.8 MPa Grade Count:62 |
Overview of materials for Polystyrene, Flame Retardant This property data is a summary of similar materials in the MatWeb database for the category "Polystyrene, Flame Retardant". Each property range of values reported is minimum and maximum values of a.. |
|||
Tensile Strength, Yield | 14.0 - 21.0 MPa | 2030 - 3050 psi | ASTM D638 |
Arkema Group KYNAR FLEX® 2750-01 Polyvinylidene Fluoride Copolymer - Extrusion & Molding Characteristics: Natural resin - translucent, off-white hemispheres. Very flexible, lubricated. High stability in harsh thermal, chemical and ultraviolet environments. High toughness and mechani.. |