- Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 111 °C
Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 111 °C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 111 °C | 232 °F | ASTM D648 |
| RheTech Products FRP257-01 32% Talc Reinforced Polypropylene Copolymer, Flame Retardant, Black Applications: Electrical component housingsConsumer goodsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 111 °C | 231 °F | ASTM D648 |
| RheTech Products RCT220-01 20% Talc Reinforced Polypropylene Copolymer, Black, Recycled Content Applications: Fan shroudsElectrical housingsHush panelsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 111 °C | 232 °F | 4 mm thick;10.0 mm wide molded rod; ISO 75/Method Bf |
| Premix Thermoplastics PRE-ELEC® PC/ABS 1420 PRE-ELEC PC/ABS 1420 is a conductive thermoplastic compound based on a PC/ABS blend. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity PR.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 111 °C @Thickness 3.20 mm |
232 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Cycoloy® CE3510 PC+ABS (Europe-Africa-Middle East) Flame retardant PC/ABS blend using non-brominated and non-chlorinated flame retardant systems, offering high impact, high heat and excellent extrusion and thermoforming characteristics. Halogen free.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 111 °C | 232 °F | 120°C/h; ISO 75/1 |
| Polykemi AB POLYfill PP CQX10030 R3 Polypropylene, Mineral Reinforced, Scratch Resistant Information provided by Polykemi AB |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 111 °C | 232 °F | 120°C/h; ISO 75/1 |
| Polykemi AB POLYfill PP CQX10030E10 F Polypropylene, Mineral Reinforced, Elastomer Modified Information provided by Polykemi AB |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 111 °C | 232 °F | 120°C/h; ISO 75/1 |
| Polykemi AB POLYfill PP CQX10030E10 Polypropylene, Mineral Reinforced, Elastomer Modified Information provided by Polykemi AB |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 111 °C | 232 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP Faradex NS0039XP PC+ABS (Europe-Africa-Middle East) LNP* FARADEX* NS0039XP is a compound based on PC/ABS resin containing Stainless Steel Fiber, Flame Retardant. Added features include: Electrically Conductive, EMI/RFI Shielding, Flame retardant.Thi.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 111 °C @Thickness 3.20 mm |
232 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics LNP Konduit MT00EL PP LNP* Konduit* MT00EL is a Polypropylene base resin with thermal fillers. Characteristics of this grade are Thermal Conductivity and it is Low Extraactible.This data was supplied by SABIC-IP for th.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 111 °C | 232 °F | ASTM D648 |
| LyondellBasell Pro-fax PD702NW Polypropylene Homopolymer, Nucleated/Antistat Primary Processing Method: Injection MoldingKey Features: nucleated and antistatic, high flow polypropylene homopolymer resin, FDA acceptable, short cycle time for high productivity, resists dust pi.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 111 °C | 232 °F | ASTM D648 |
| Flint Hills P4C6B-134A Polypropylene Homopolymer Features: Excellent processability, nucleated and antistat. Product does not contain animal derived components. Phthalate-free.Applications: Injection Molding: Cutlery, Consumer Products, Cosmetic.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 111 °C | 232 °F | ISO 75-1,-2 |
| Ineos ABS Lustran® ABS 150G22 20% Glass Fiber Reinforced Grade |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 111 °C | 232 °F | ASTM D648-97 |
| Ipiranga Petrochem PCC 2314 Polypropylene The production of polypropylene (PP) employs Spheripol technology from Montell / Italy. This technology has been acclaimed all over the world and is known as clean technology, because it does not pr.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 111 °C | 232 °F | ASTM D648 |
| LyondellBasell Astryn 65F4-3 Polypropylene Homopolymer, 30% Talc Key Features: conventional melt flow, very high modulus, mineral-filled polypropylene homopolymer, excellent heat resistance, high stiffness, excellent chemical resistance, good surface qualityAppli.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 111 °C @Thickness 3.20 mm |
232 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP LUBRICOMP ML003S PP LNP* LUBRICOMP* ML003S is a compound based on Polypropylene resin containing 15% PTFE. Added features include: Heat Stabilized, Wear Resistant. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 111 °C @Thickness 6.40 mm |
232 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP STAT-KON Noryl_HMC1010 PPE+HIPS (Europe-Africa-Middle East) LNP* Stat-kon* HMC1010 compound is a 10% Carbon fiber reinforced. Static dissipative. Nonbrominated, nonchlornated flame retardant system. UL94 V-1 rated. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 111 °C @Thickness 6.40 mm |
232 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP STAT-KON Noryl_HMC1010 PPE+PS LNP* Stat-kon* Noryl_HMC1010 compound is a 10% Carbon fiber reinforced. Static dissipative. Nonbrominated, nonchlor- nated flame retardant system. UL94 V-1 rated. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 111 °C @Thickness 3.20 mm |
232 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Xenoy® X2420 PC+POLYESTER (Asia Pacific) Xenoy*X2420 is a 10% glass filled, high flow, impact modified, injection moldable grade designed for high flow and impact strength. X2420 has enhanced melt flowability, impact ductility and broad co.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 111 °C | 232 °F | ISO 75 |
| Styrolution Novodur® HH-106 ABS Novodur HH-106 is a high heat injection molding grade providing a balanced property profile.Information provided by Styrolution |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 111 °C | 232 °F | ISO 75 |
| Styrolution Terluran® HH-106 ABS Terluran HH-106 is an injection molding ABS grade with high resistance to heat deformation and impact.Information provided by STYROLUTION, which is a joint venture between BASF and INEOS. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 111 °C | 232 °F | ISO 75 |
| Styrolution Terluran® HH-106 Q109 Colored ABS Description: Injection-molding grade with high resistance to heat deformation and impact, with improved surface quality suitable for automotive applications.Information provided by STYROLUTION, whic.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 111 °C | 232 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP THERMOCOMP ZF0049 PPE+PS (Asia Pacific) LNP* Thermocomp* ZF0049 is a compound based on PPE+PS Blend resin containing Flame Retardant. Added features of this material include: Flame Retardant. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 111 °C | 232 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP THERMOCOMP ZF0049 PPE+PS LNP* THERMOCOMP* ZF0049 is a compound based on PPE+PS resin containing 20% Glass Fiber. Added feature of this material is: Flame Retardant. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 111 °C | 232 °F | ISO 75-1/-2 |
| DuPont Performance Polymers Delrin® 100STE NC010 Acetal (POM)
(Unverified Data**) Super Toughened High Viscosity Acetal Homopolymer with Very Low Emissions Delrin 100STE NC010 (formerly DE20590) is a high-viscosity super-toughened acetal homopolymer with very low VOC emissions. P.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 111 °C | 232 °F | Unannealed; ASTM D648 |
| Dow C700-35N Polypropylene Impact Copolymer Resin OverviewGood mold fillabilityHigh stiffnessFast set-upContains a nucleating additiveComplies with: U.S. FDA FCN 843, Canadian HPFB No ObjectionDOW C700-35N Polypropylene Resin is intended for use in.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 111 °C | 232 °F | ASTM D648B |
| Braskem FF450WV Homopolymer Polypropylene Description: Excellent Processability, Nucleated.Applications: Suggested Uses Include Fast-Cycle Injection Molding and CompoundingProcess: Injection Molding.This resin meets the requirements for ole.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 111 °C | 232 °F | ASTM D648 |
| Aclo Accutech Polypropylene Copolymer CP0436W30L Wollastonite Reinforced |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 111 °C | 232 °F | ASTM D648 |
| Cheng Yu Plastic A707G25 SAN, 25% Glass Fiber |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 111 °C | 232 °F | 0.125 inch; ASTM D648 |
| PlastxWorld CEVIAN®-V 400N ABS Heat Resistant ABSThese are typical values and are not intended for specification purposes. UL approved file No. is E47773. Information provided by PlastxWorld Inc. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 111 °C | 232 °F | ASTM D648 |
| Adell EZ-18 Homopolymer Polypropylene, 40% Calcium Carbonate Filled Data provided by Adell Plastics, Inc. |
|||