SABIC Innovative Plastics Cycoloy® MC5215 PC+ABS
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Cycoloy® |
| Port | Shanghai port,China |
| Trade Terms | EXW, FOB, CFR, CIF |
| Payment Terms | L/C, T/T, PayPal |
| Download PDF | SABIC Innovative Plastics Cycoloy® MC5215 PC+ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.29 g/cc | 0.0466 lb/in³ | ASTM D792 |
| Water Absorption at Saturation | 0.15 % | 0.15 % | ISO 62 |
| Melt Flow | 20 g/10 min <br>@Load 2.16 kg,<br> Temperature 260 °C |
20 g/10 min <br>@Load 4.76 lb,<br> Temperature 500 °F |
ASTM D1238 |
| Melt Index of Compound | 17 g/10 min <br>@Load 2.16 kg,<br> Temperature 260 °C |
17 g/10 min <br>@Load 4.76 lb,<br> Temperature 500 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 86.0 MPa | 12500 psi | Type I, 5 mm/min; ASTM D638 |
| 86.0 MPa | 12500 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 2.5 % | 2.5 % | 5 mm/min; ISO 527 |
| 2.7 % | 2.7 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 5.77 GPa | 837 ksi | 5 mm/min; ASTM D638 |
| 5.91 GPa | 857 ksi | 1 mm/min; ISO 527 | |
| Flexural Yield Strength | 134 MPa | 19400 psi | 2 mm/min; ISO 178 |
| 135 MPa | 19600 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 4.97 GPa | 721 ksi | 2 mm/min; ISO 178 |
| 5.15 GPa | 747 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.700 J/cm | 1.31 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched (ISO) | 32.0 kJ/m² | 15.2 ft-lb/in² | 80*10*3; ISO 180/1U |
| 7.00 kJ/m² <br>@Temperature -30.0 °C |
3.33 ft-lb/in² <br>@Temperature -22.0 °F |
80*10*3; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 95.0 °C <br>@Thickness 3.20 mm |
203 °F <br>@Thickness 0.126 in |
unannealed; ASTM D648 |
| Vicat Softening Point | 100 °C | 212 °F | Rate B/120; ISO 306 |
| Flammability, UL94 | V-1 <br>@Thickness 1.50 mm |
V-1 <br>@Thickness 0.0591 in |
UL 94 |
Users viewing this material also viewed the following:
- NOVA Chemicals Novapol® LF-0225-B LDPE Clarity Film Resin (discontinued **)
- I. Stern 728 High Gloss Medium Natural ABS
- Mearthane Durethaneâ„¢ S DS-555D Solid Polyurethane Elastomer
- Solvay Specialty Polymers Amodel® A-4133 HH Polyphthalamide (PPA), 33% Glass Fiber (Conditioned)
- Sanyo PELESTAT® NC7530 Antistatic Additive
- Samsung Cheil Industries Infino® HI-1001BN PC/ABS, Unreinforced
- A. Schulman POLYTROPE™ TPP 402 Blow Molding Grade Olefinic Thermoplastic Elastomer
- DuPont™ Appeel® 22D843 Ethylene Acrylate
- Solvay RHODISOLV® GREEN 25 Solvent
- NOVA Chemicals Novapol® TF-Y826-BP Hexene LLDPE Film Resin (discontinued **)
Copyright © lookpolymers.com All Rights Reserved