Ravago Manufacturing Americas Hylon® N1000NL Nylon 6/6 (Cond)  (discontinued **)

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Unreinforced
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Ravago Manufacturing Americas Hylon® N1000NL Nylon 6/6 (Cond)  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Entec's proprietary products include a full range of compounds in the Nylon 6/6, Nylon 6, ABS, PBT, Polycarbonate, PC/ABS, PC/ASA, PC/PBT, and PPO/PPE resin families.Information provided by Ravago.
Physical Properties Metric English Comments
Density 1.14 g/cc
0.0412 lb/in³
DAM; ASTM D792
Water Absorption 1.1 %
1.1 %
24 hrs, DAM; ASTM D570
Linear Mold Shrinkage 0.012 cm/cm
0.012 in/in
0.125 in, DAM; ASTM D955
Mechanical Properties Metric English Comments
Hardness, Rockwell M 64
64
ASTM D785
Tensile Strength at Break 72.4 MPa
10500 psi
ASTM D638
Elongation at Break 35 %
35 %
ASTM D638
Flexural Strength 62.1 MPa
9000 psi
ASTM D790
Flexural Modulus 1.65 GPa
240 ksi
ASTM D790
Izod Impact, Notched 1.23 J/cm
2.30 ft-lb/in
73°F; ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 235 °C
455 °F
Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 82.2 °C
180 °F
Unannealed; ASTM D648
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+12 ohm-cm
1.00e+12 ohm-cm
ASTM D257
Dielectric Constant 7.0

@Frequency 100 Hz
7.0

@Frequency 100 Hz
ASTM D150
Dielectric Strength 21.5 kV/mm
545 kV/in
ASTM D149
Processing Properties Metric English Comments
Melt Temperature 271 - 293 °C
520 - 560 °F
Mold Temperature 48.9 - 93.3 °C
120 - 200 °F
Drying Temperature 73.9 °C
165 °F
Dry Time 2 - 4 hour
2 - 4 hour
Moisture Content 0.20 %
0.20 %
Back Pressure 0.345 - 0.689 MPa
50.0 - 100 psi
Screw Speed 40 - 140 rpm
40 - 140 rpm