Styron EMERGEâ„¢ 7500 Polycarbonate (PC) / Acrylonitrile Butadiene Styrene (ABS)

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate (PC)
Manufacturer Styron
Trade Name EMERGE™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Styron EMERGEâ„¢ 7500 Polycarbonate (PC) / Acrylonitrile Butadiene Styrene (ABS).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
EMERGEâ„¢ PC/ABS 7500 advanced resin is an ignition-resistant PC/ABS blend that contains no chlorine or bromine additives. This resin is suitable for use in a wide variety of applications in the information technology equipment market.Information provided by DowThis product line was spun off from Dow Chemical to Styron in 2010.
Physical Properties Metric English Comments
Linear Mold Shrinkage 0.0040 - 0.0060 cm/cm
0.0040 - 0.0060 in/in
ISO 294-4/D2
Melt Flow 12 g/10 min

@Load 3.80 kg,
Temperature 230 °C
 12 g/10 min

@Load 8.38 lb,
Temperature 446 °F
 ISO 1133
55 g/10 min

@Load 5.00 kg,
Temperature 260 °C
 55 g/10 min

@Load 11.0 lb,
Temperature 500 °F
 ISO 1133
Mechanical Properties Metric English Comments
Hardness, Rockwell R 122
122
ISO 2039/2
Tensile Strength at Break 45.0 MPa

@Thickness 4.00 mm
 6530 psi

@Thickness 0.157 in
 50mm/min, injection molded, unannealed; ISO 527-2
Tensile Strength, Yield 60.0 MPa

@Thickness 4.00 mm
 8700 psi

@Thickness 0.157 in
 50mm/min, injection molded, unannealed; ISO 527-2
Elongation at Break 75 %

@Thickness 4.00 mm
 75 %

@Thickness 0.157 in
 50mm/min, injection molded, unannealed; ISO 527-2
Elongation at Yield 4.5 %

@Thickness 4.00 mm
 4.5 %

@Thickness 0.157 in
 50mm/min, injection molded, unannealed; ISO 527-2
Flexural Strength 90.0 MPa

@Thickness 4.00 mm
 13100 psi

@Thickness 0.157 in
 2mm/min, injection molded, unannealed; ISO 178
Flexural Modulus 2.40 GPa

@Thickness 4.00 mm
 348 ksi

@Thickness 0.157 in
 2mm/min, injection molded, unannealed; ISO 178
Izod Impact, Notched (ISO) 35.0 kJ/m²
16.7 ft-lb/in²
ISO 180/A
Charpy Impact, Notched 3.00 J/cm²
14.3 ft-lb/in²
ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear 67.0 µm/m-°C

@Temperature 20.0 °C
 37.2 µin/in-°F

@Temperature 68.0 °F
 ASTM D696
Deflection Temperature at 0.46 MPa (66 psi) 97.0 °C
207 °F
ISO 75-2 Bf
Deflection Temperature at 1.8 MPa (264 psi) 87.0 °C
189 °F
ISO 75-2 Af
Vicat Softening Point 102 °C
216 °F
50°C / 50N; ISO 306 B 50
112 °C
234 °F
120°C / 10N; ISO 306 A 120
Flammability, UL94 V-0

@Thickness 1.50 mm
 V-0

@Thickness 0.0591 in
V-0

@Thickness 2.00 mm
 V-0

@Thickness 0.0787 in
Oxygen Index 30 %
30 %
ISO 4589
Processing Properties Metric English Comments
Melt Temperature 240 - 270 °C
464 - 518 °F
Mold Temperature 60.0 - 90.0 °C
140 - 194 °F
Drying Temperature 80.0 - 90.0 °C
176 - 194 °F
Dry Time 3 - 4 hour
3 - 4 hour