Polymer Property : Tensile Strength at Break = 10500 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength at Break 72.4 MPa
10500 psi
2 in/min; ASTM D638
RheTech Products F56-01 40% Glass Fiber/Mineral Co-Reinforced Polypropylene, Chemically Coupled, Black
Applications: Consumer goodsUnderhood componentsInjection molding conditions reported in table.Information provided by RheTech Products.
Tensile Strength at Break 72.4 MPa
10500 psi
2 in/min; ASTM D638
RheTech Products G40P100-01 40% Glass Fiber Reinforced Polypropylene, Black
Injection molding conditions reported in table.Information provided by RheTech Products.
Tensile Strength at Break 72.4 MPa
10500 psi
2 in/min; ASTM D638
RheTech Products GC30P105-08FA 30% Glass Fiber Reinforced Polypropylene, Chemically Coupled, FDA Compliant, Black
Applications: Water system housingFDA approved partsInjection molding conditions reported in table.Information provided by RheTech Products.
Tensile Strength at Break 72.4 MPa
10500 psi
Type I, 5.1 mm/min; ASTM D638
PolyOne Nymax™ MF 1204 40 Black 13 Polyamide 66 (Nylon 66)
The Nymax® MF 1200 Series of mineral-reinforced nylon 6/6 compounds have been specifically engineered to provide an excellent balance of physical property performance, toughness, chemical resistanc..
Tensile Strength at Break 72.4 MPa
10500 psi
ASTM D638
Niche Polymer PPHG20BK Homopolymer PP, 20% Glass Fiber Filled
Information provided by Niche Polymer
Tensile Strength at Break 72.4 MPa
10500 psi
ASTM D638
Polymer Resources PC-GP1-[color]-LF Polycarbonate, General Purpose, Food Contact
Polycarbonate, General Purpose, Low FlowFeatures: • Food Contact AcceptableProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, ..
Tensile Strength at Break 72.4 MPa
10500 psi
ASTM D638
Polymer Resources PC-GP1-D-[color]-1 Polycarbonate, General Purpose, Low Flow with Mold Release
Polycarbonate, General Purpose, Low Flow with Mold ReleaseProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Inform..
Tensile Strength at Break 72.4 MPa
10500 psi
ASTM D638
Polymer Resources PC-GP1-D-[color]-6 Polycarbonate, FDA-compliant Feedstocks, Low Flow with Mold Release
Polycarbonate, FDA-compliant Feedstocks, Low Flow with Mold ReleaseProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test sampl..
Tensile Strength at Break 72.4 MPa
10500 psi
ASTM D638
Polymer Resources PC-UV1-D-[color]-1 Polycarbonate, UV-stabilized, Low Flow with Mold Release
Polycarbonate, UV-stabilized, Low Flow with Mold ReleaseProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Informat..
Tensile Strength at Break 72.4 MPa
10500 psi
ASTM D638
Polymer Resources PPX-G10 Modified-PPO, 10% Glass Reinforced
Modified-Polyphenylene Oxide, 10% Glass ReinforcedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information pr..
Tensile Strength at Break 72.4 MPa
10500 psi
ASTM D638
Ravago Manufacturing Americas Hylon® N1000NL2 Nylon 6/6 (Cond)
Information provided by Ravago.
Tensile Strength at Break 72.4 MPa
10500 psi
ASTM D638
M. Holland Company PC406UR Polycarbonate
High impact resistanceGood mold releaseGood UV resistanceHigh viscosityApplications: AppliancesProtective coveringsDecorative displaysHousings
Tensile Strength at Break 72.4 MPa
10500 psi
ASTM D638
Techmer ES Plaslube® J-50/10/TF/15 BK223 Polycarbonate
Tensile Strength at Break 72.4 MPa
10500 psi
50 mm/min; ASTM D638
Styron CALIBREâ„¢ 301-6 Polycarbonate Resin
Overview: CALIBREâ„¢ 300-6 polycarbonate resins offer exceptional impact resistance, heat distortion resistance and optical clarity as well as high melt strength for blow molding and sheet applic..
Tensile Strength at Break 72.4 MPa
10500 psi
50 mm/min; ASTM D638
Styron CALIBREâ„¢ 302V-6 Polycarbonate Resin
Overview: CALIBREâ„¢ 302V-6 Polycarbonate resins offer exceptional impact resistance, heat distortion resistance and optical clarity (for tinted/transparent colors), and is available in both tint..
Tensile Strength at Break 72.4 MPa
10500 psi
ASTM D638
Chase Plastics CP Pryme® A120 ABS, 20% Glass Fiber Reinforced
Features: Glass fiber reinforcementInjection moldingForm: PelletsInformation provided by Chase Plastics.
Tensile Strength at Break 72.4 MPa
10500 psi
ASTM D638
Chase Plastics CP Pryme® A220G ABS Molding Resin, 20% Glass Fiber Reinforced
Information provided by Chase Plastics.
Tensile Strength at Break 72.4 MPa
10500 psi
ASTM D3574
3M 436 Vibration Damping Tape
3M™ Vibration Damping Tapes are low temperature 3M™ Viscoelastic Damping Polymers Tape 830 coated on the dead soft aluminum foil constraining layer. They have pressure sensitive properties and are..