PolyOne Versollan™ OM 1262NX-9 Thermoplastic Elastomer (TPE)

Category	Polymer , Thermoplastic , Elastomer, TPE
Manufacturer	PolyOne Corporation
Trade Name	Versollan™
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	PolyOne Versollan™ OM 1262NX-9 Thermoplastic Elastomer (TPE).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Versollan™ OM 1262NX-9 is a performance TPU alloy designed for thin-wall overmolding onto polycarbonate (PC), ABS, PC/ABS and copolyester substrates. - Excellent Grip with Matte, Rubbery Finish - Proven Track Record - Superior Adhesion to PC, ABS, PC/ABS, PC/PBT and CopolyesterPurge thoroughly before and after use of this product with a low flow (0.5 - 2.5 MFR) polyethylene (PE) or polypropylene (PP). Regrind levels up to 20% can be used with Versollan™ OM 1262NX-9 with minimal property loss, provided that the regrind is free of contamination. To minimize losses during molding, the melt temperature should remain as low as possible. The final determination of regrind effectiveness should be determined by the customer. Versollan™ OM 1262NX-9 should not be left in the barrel for extended idle periods (greater than 5 minutes). Suggested Dewpoint: -40°F Injection Speed: 1 to 5 in/sec 1st Stage - Boost Pressure: 200 to 800 psi 2nd Stage - Hold Pressure: 70% of Boost Hold Time (Thick Part): 4 to 10 sec Hold Time (Thin Part): 1 to 3 secInformation provided by PolyOne

Physical Properties	Metric	English	Comments
Specific Gravity	1.17 g/cc	1.17 g/cc	ASTM D792
Viscosity	19900 cP @Shear Rate 11200 1/s, Temperature 200 °C	19900 cP @Shear Rate 11200 1/s, Temperature 392 °F	ASTM D3835
Maximum Moisture Content	0.020 - 0.030	0.020 - 0.030
Linear Mold Shrinkage, Flow	0.0090 - 0.015 cm/cm	0.0090 - 0.015 in/in	ASTM D955
Melt Flow	7.0 g/10 min @Load 2.16 kg, Temperature 190 °C	7.0 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238
	100 g/10 min @Load 5.00 kg, Temperature 200 °C	100 g/10 min @Load 11.0 lb, Temperature 392 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	65	65	10 sec; ASTM D2240
Tensile Strength at Break	7.64 MPa @Temperature 23.0 °C	1110 psi @Temperature 73.4 °F	Die C2 hr; ASTM D412
Tensile Stress	2.55 MPa @Strain 100 %, Temperature 23.0 °C	370 psi @Strain 100 %, Temperature 73.4 °F	Die C2 hr; ASTM D412
	3.34 MPa @Strain 300 %, Temperature 23.0 °C	484 psi @Strain 300 %, Temperature 73.4 °F	Die C2 hr; ASTM D412
Elongation at Break	710 % @Temperature 23.0 °C	710 % @Temperature 73.4 °F	Die C2 hr; ASTM D412
Tear Strength	40.3 kN/m	230 pli	ASTM D624
Compression Set	35 % @Temperature 23.0 °C, Time 79200 sec	35 % @Temperature 73.4 °F, Time 22.0 hour	ASTM D395B

Thermal Properties	Metric	English	Comments
Flammability, UL94	HB @Thickness 1.50 mm	HB @Thickness 0.0591 in	UL 94

Processing Properties	Metric	English
Rear Barrel Temperature	163 - 185 °C	325 - 365 °F
Middle Barrel Temperature	168 - 196 °C	334 - 385 °F
Front Barrel Temperature	177 - 210 °C	351 - 410 °F
Nozzle Temperature	177 - 210 °C	351 - 410 °F
Mold Temperature	21.1 - 48.9 °C	70.0 - 120 °F
Drying Temperature	51.7 - 54.4 °C	125 - 130 °F
Dry Time	3.00 - 4.00 hour	3.00 - 4.00 hour
Back Pressure	0.172 - 0.345 MPa	24.9 - 50.0 psi
Screw Speed	25 - 75 rpm	25 - 75 rpm

Descriptive Properties	Value	Comments
Agency Ratings	UL 94 .QMFZ2.E76261
Appearance	Black
Features	Good Moldability
	Good Processability
	Low Gloss
Forms	Pellets
Generic Material	TPE
Generic Name	Thermoplastic Elastomer (TPE)
Manufacturer / Supplier	GLS Thermoplastic Elastomers
Processing Method	Injection Molding
Regional Availability	Africa & Middle East
	Asia Pacific
	Europe
	North America
	South America
RoHS Compliance	RoHS Compliant
Suggested Max Regrind	20%
Uses	Business Equipment
	Consumer Applications
	Electrical/Electronic Applications
	Flexible Grips
	Overmolding
	Power/Other Tools
	Thin-walled Parts