PolyOne Versaflex™ HC 2110-57B Thermoplastic Elastomer (TPE)

Category	Polymer , Thermoplastic , Elastomer, TPE
Manufacturer	PolyOne Corporation
Trade Name	Versaflex™
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	PolyOne Versaflex™ HC 2110-57B Thermoplastic Elastomer (TPE).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Versaflex™ HC 2110-57B is a TPE designed for use in the healthcare industry offering low stiction and good compression set. New Product. Commercial specifications have not been established. - Bonds to Polypropylene - ETO sterilizable and AutoclavablePurge thoroughly before and after use of this product with a low flow (0.5 - 2.5 MFR) polyethylene (PE) or polypropylene (PP). Versaflex™ HC 2110-57B has excellent melt stability. Maximum residence times may vary, depending on the size of the barrel. Generally, the barrel should be emptied if it is idle for periods of 8 - 10 minutes or longer. Drying is not Required Injection Speed: 0.5 to 2.5 in/sec Hold Time (Thick Part): 2 to 7 sec Hold Time (Thin Part): 1 to 3 secInformation provided by PolyOne

Physical Properties	Metric	English	Comments
Specific Gravity	1.01 g/cc	1.01 g/cc	ASTM D792
Viscosity	7.70e+6 cP @Shear Rate 11200 1/s, Temperature 200 °C	7.70e+6 cP @Shear Rate 11200 1/s, Temperature 392 °F	ASTM D3835
Linear Mold Shrinkage, Flow	0.0070 - 0.012 cm/cm	0.0070 - 0.012 in/in	ASTM D955

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	59 @Temperature 23.0 °C	59 @Temperature 73.4 °F	10 sec; ASTM D2240
Tensile Strength at Break	3.70 MPa @Temperature 23.0 °C	537 psi @Temperature 73.4 °F	Die C2 hr; ASTM D412
Tensile Stress	2.54 MPa @Strain 100 %, Temperature 23.0 °C	368 psi @Strain 100 %, Temperature 73.4 °F	Die C2 hr; ASTM D412
	3.85 MPa @Strain 300 %, Temperature 23.0 °C	558 psi @Strain 300 %, Temperature 73.4 °F	Die C2 hr; ASTM D412
Elongation at Break	350 % @Temperature 23.0 °C	350 % @Temperature 73.4 °F	Die C2 hr; ASTM D412
Tear Strength	25.7 kN/m	147 pli	ASTM D624
Compression Set	20 % @Temperature 21.0 °C, Time 79200 sec	20 % @Temperature 69.8 °F, Time 22.0 hour	ASTM D395B
	28 % @Temperature 70.0 °C, Time 79200 sec	28 % @Temperature 158 °F, Time 22.0 hour	ASTM D395B
	37 % @Temperature 100 °C, Time 79200 sec	37 % @Temperature 212 °F, Time 22.0 hour	ASTM D395B

Processing Properties	Metric	English
Rear Barrel Temperature	166 - 182 °C	331 - 360 °F
Middle Barrel Temperature	193 - 216 °C	379 - 421 °F
Front Barrel Temperature	204 - 227 °C	399 - 441 °F
Nozzle Temperature	204 - 232 °C	399 - 450 °F
Mold Temperature	12.8 - 32.2 °C	55.0 - 90.0 °F
Screw Speed	80 - 120 rpm	80 - 120 rpm

Descriptive Properties	Value	Comments
Agency Ratings	ISO 10993 Part 4
	ISO 10993 Part 5
	USP Class VI
Appearance	Black
Features	Good Sterilizability
	Low Compression Set
	Low Friction
Forms	Pellets
Generic Material	TPE
Generic Name	Thermoplastic Elastomer (TPE)
Manufacturer / Supplier	GLS Thermoplastic Elastomers
Processing Method	Injection Molding
Regional Availability	Africa & Middle East
	Asia Pacific
	Europe
	North America
	South America
RoHS Compliance	RoHS Compliant
Uses	Gaskets
	Medical/Healthcare Applications
	Overmolding
	Plugs