- PlastiComp Complet® LCF50 - TPU Rigid Thermoplastic Polyurethane, 50% Long Carbon Fiber Reinforced
PlastiComp Complet® LCF50 - TPU Rigid Thermoplastic Polyurethane, 50% Long Carbon Fiber Reinforced
| Category | Polymer , Thermoplastic , Polyurethane, TP , Thermoplastic Polyurethane (TPUR), Carbon Fiber Reinforced |
| Manufacturer | PlastiComp |
| Trade Name | Complēt® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PlastiComp Complet® LCF50 - TPU Rigid Thermoplastic Polyurethane, 50% Long Carbon Fiber Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Complet® long-fiber reinforced pellets are manufactured to exceed expectation for quality and performance.Polyurethane with 50% carbon fiber reinforcementInformation provided by PlastiComp, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.43 g/cc | 1.43 g/cc | ASTM D-792 |
| Filler Content | 50 % | 50 % | Carbon Fiber |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 256 MPa | 37100 psi | ASTM D-638 |
| Elongation at Break | 1.0 - 2.0 % | 1.0 - 2.0 % | ASTM D-638 |
| Tensile Modulus | 37.034 GPa | 5371.3 ksi | ASTM D-638 |
| Flexural Strength | 432 MPa | 62700 psi | ASTM D-790 |
| Flexural Modulus | 33.103 GPa | 4801.2 ksi | ASTM D-790 |
| Izod Impact, Notched | 3.20 J/cm | 5.99 ft-lb/in | ASTM D-256 |
| Izod Impact, Unnotched | 9.078 J/cm | 17.01 ft-lb/in | ASTM D-4812 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 113 °C | 235 °F | ASTM D-648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 204 - 227 °C | 400 - 440 °F | |
| Middle Barrel Temperature | 210 - 232 °C | 410 - 450 °F | |
| Front Barrel Temperature | 216 - 238 °C | 420 - 460 °F | |
| Nozzle Temperature | 221 - 243 °C | 430 - 470 °F | |
| Melt Temperature | 216 - 238 °C | 420 - 460 °F | |
| Mold Temperature | 87.8 °C | 190 °F | |
| Injection Velocity | 50.8 - 76.2 mm/sec | 2.00 - 3.00 in/sec | |
| Drying Temperature | 88.0 °C @Time 14400 sec |
190 °F @Time 4.00 hour |
|
| Moisture Content | <= 0.020 % | <= 0.020 % | |
| Back Pressure | 0.172 - 0.345 MPa | 25.0 - 50.0 psi | |
| Cushion | 0.635 cm | 0.250 in | |
| Screw Speed | 30 - 50 rpm | 30 - 50 rpm |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Injection Pressure | Medium to maximum |