Omnia Plastica ABS Acrylonitrile-butadiene-styrene

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Extruded
Manufacturer Omnia Plastica s.p.a.
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Omnia Plastica ABS Acrylonitrile-butadiene-styrene.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Acrylonitrile-butadiene-styrene is an amorphous thermopolymer used largely for injection moulded items. The stock shapes are mainly used for the production of prototypes.Features:Good machinability Polishing: to obtain aesthetic pieces Easy bonding Colour: naturalWeak Point:Poor mechanical and ageing properties, low abrasion resistance.Application:Prototypes: for various industrial fields Mechanical: it has no mechanical properties. Food contact: if natural it can be used in contact with food. Chemical: the chemical resistance is poor. It is not used for this purpose.Information provided by Omnia Plastica s.p.a. for semifinished products such as sheet, rod, and tube.
Physical Properties Metric English Comments
Density 1.06 g/cc
0.0383 lb/in³
ISO.1183 DIN.53479
Moisture Absorption at Equilibrium 0.00 %
0.00 %
50% relative humidity
Water Absorption at Saturation 0.70 %
0.70 %
23°C
Mechanical Properties Metric English Comments
Hardness, Rockwell M 82
82
dry sample; ISO2039.2
Ball Indentation Hardness 85.0 MPa
12300 psi
ISO2039.1 DIN.53456
Tensile Strength at Break 45.0 MPa
6530 psi
ISO.527 DIN.53455
Elongation at Break 25 %
25 %
ISO.527 DIN.53455
Tensile Modulus 2.50 GPa
363 ksi
ISO.527 DIN.53455
Compressive Strength 17.0 MPa
2470 psi
1% strain over 1000 hours; ISO.899 DIN.53444
Charpy Impact Unnotched NB
NB
7.5 J; ISO.R179 DIN.53453
Charpy Impact, Notched 1.40 J/cm²
6.66 ft-lb/in²
ISO179/3C DIN.53453
Coefficient of Friction, Dynamic 0.50
0.50
on dry ground steel; load =0.05MPa; speed =0.6 m/s
Thermal Properties Metric English Comments
CTE, linear 90.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
50.0 µin/in-°F

@Temperature 73.4 - 140 °F
Thermal Conductivity 0.150 W/m-K
1.04 BTU-in/hr-ft²-°F
DIN.52612
Maximum Service Temperature, Air 90.0 °C
194 °F
Maximum operating temperature continuously for 5000 hours based on a tensile stress of 50% at 23° C.
100 °C
212 °F
short period, no load
Deflection Temperature at 1.8 MPa (264 psi) 85.0 °C
185 °F
ISO.75 DIN.53461
Minimum Service Temperature, Air -20.0 °C
-4.00 °F
impact conditions and heavy loads not considered
Flammability, UL94 HB
HB
Oxygen Index 19 %
19 %
ISO.4589
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+16 ohm-cm
1.00e+16 ohm-cm
ISO.93 DIN.53482
Dielectric Constant 3.3

@Frequency 1e+6 Hz
3.3

@Frequency 1e+6 Hz
ISO.250 DIN.53483
Dielectric Strength 20.0 kV/mm
508 kV/in
ISO.243 DIN.53481
Dissipation Factor 0.020

@Frequency 1e+6 Hz
0.020

@Frequency 1e+6 Hz
ISO.250 DIN.53483
Descriptive Properties Value Comments
Form Amorphous