NOVA Chemicals Novapol® LF-Y819-C LDPE Film Resin

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Film Grade
Manufacturer NOVA Chemicals
Trade Name Novapol®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF NOVA Chemicals Novapol® LF-Y819-C LDPE Film Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Film Properties. Features: Good strength and toughness, excellent shrink film characteristics, excellent processability.Applications: Industrial packaging, liners, shrink film, blends with LLDPE.Data provided by the manufacturer.
Physical Properties Metric English Comments
Density 0.920 g/cc
0.0332 lb/in³
ASTM D792
Thickness 38.1 microns
1.50 mil
Melt Flow 0.75 g/10 min

@Load 2.16 kg,
Temperature 190 °C
0.75 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 11.0 MPa
1600 psi
ASTM D882
Film Tensile Strength at Yield, TD 10.0 MPa
1450 psi
ASTM D882
Film Elongation at Break, MD 400 %
400 %
ASTM D882
Film Elongation at Break, TD 600 %
600 %
ASTM D882
Secant Modulus, MD 0.180 GPa
26.1 ksi
ASTM D882
Secant Modulus, TD 0.200 GPa
29.0 ksi
ASTM D882
Coefficient of Friction >= 0.40
>= 0.40
ASTM D1894
Elmendorf Tear Strength, MD 7.50 g/micron
191 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 3.50 g/micron
88.9 g/mil
ASTM D1922
Dart Drop 3.00 g/micron
76.2 g/mil
F 50; ASTM D1709/A
Film Tensile Strength at Break, MD 20.0 MPa
2900 psi
ASTM D882
Film Tensile Strength at Break, TD 18.0 MPa
2610 psi
ASTM D882
Optical Properties Metric English Comments
Haze 17 %

@Thickness 0.0250 mm
17 %

@Thickness 0.000984 in
ASTM D1003
Gloss 35 %
35 %
45°; 1 mil; ASTM D1894
Processing Properties Metric English Comments
Melt Temperature 170 - 190 °C
338 - 374 °F