Lanxess Durethan® BKV 30 G H2.0 900116 Nylon 6, 30% Glass Fiber

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled
Manufacturer Lanxess
Trade Name Durethan®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Lanxess Durethan® BKV 30 G H2.0 900116 Nylon 6, 30% Glass Fiber.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PA 6, injection molding grade, 30% glass fibers, better surface finish and resistance to alcoholic calcium chloride-solution than BKV 30 H2.0, heat-stabilized, good heat-ageing resistance
Physical Properties Metric English Comments
Density 1.36 g/cc
0.0491 lb/in³
ISO 1183
Water Absorption 6.5 %
6.5 %
Test Sim. to ISO 62
Moisture Absorption at Equilibrium 1.9 %
1.9 %
23°C/50% R.H.; Test Sim. to ISO 62
Viscosity Test 140 cm³/g
140 cm³/g
Viscosity number; ISO 307, 1157, 1628
Linear Mold Shrinkage, Flow 0.0027 cm/cm
0.0027 in/in
ISO 294-4, 2577
Linear Mold Shrinkage, Transverse 0.0058 cm/cm
0.0058 in/in
ISO 294-4, 2577
Mechanical Properties Metric English Comments
Tensile Strength at Break 110 MPa
16000 psi
Conditioned; ISO 527-1/-2
180 MPa
26100 psi
ISO 527-1/-2
Elongation at Break 3.0 %
3.0 %
ISO 527-1/-2
7.0 %
7.0 %
Conditioned; ISO 527-1/-2
Tensile Modulus 6.20 GPa
899 ksi
Conditioned; ISO 527-1/-2
9.50 GPa
1380 ksi
ISO 527-1/-2
Charpy Impact Unnotched 6.00 J/cm²

@Temperature -30.0 °C
28.6 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eU
6.00 J/cm²

@Temperature -30.0 °C
28.6 ft-lb/in²

@Temperature -22.0 °F
Conditioned; ISO 179/1eU
7.50 J/cm²

@Temperature 23.0 °C
35.7 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eU
7.50 J/cm²

@Temperature 23.0 °C
35.7 ft-lb/in²

@Temperature 73.4 °F
Conditioned; ISO 179/1eU
Charpy Impact, Notched <= 1.00 J/cm²

@Temperature -30.0 °C
<= 4.76 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eA
<= 1.00 J/cm²

@Temperature -30.0 °C
<= 4.76 ft-lb/in²

@Temperature -22.0 °F
Conditioned; ISO 179/1eA
1.00 J/cm²

@Temperature 23.0 °C
4.76 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA
1.30 J/cm²

@Temperature 23.0 °C
6.19 ft-lb/in²

@Temperature 73.4 °F
Conditioned; ISO 179/1eA
Impact 838
838
Puncture maximum force (N); ISO 6603-2
735

@Temperature -30.0 °C
735

@Temperature -22.0 °F
Puncture maximum force (N); ISO 6603-2
Puncture Energy 2.60 J
1.92 ft-lb
ISO 6603-2
2.20 J

@Temperature -30.0 °C
1.62 ft-lb

@Temperature -22.0 °F
ISO 6603-2
2.20 J

@Temperature -30.0 °C
1.62 ft-lb

@Temperature -22.0 °F
Conditioned; ISO 6603-2
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 30.0 µm/m-°C
16.7 µin/in-°F
ISO 11359-1/-2
CTE, linear, Transverse to Flow 80.0 µm/m-°C
44.4 µin/in-°F
ISO 11359-1/-2
Melting Point 221 °C
430 °F
10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi) 215 °C
419 °F
ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 195 °C
383 °F
ISO 75-1/-2
Deflection Temperature at 8.0 MPa 80.0 °C
176 °F
ISO 75-1/-2
Vicat Softening Point 210 °C
410 °F
50°C/h 50N; ISO 306
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
IEC 60695-11-10
HB

@Thickness 3.20 mm
HB

@Thickness 0.126 in
IEC 60695-11-10
Oxygen Index 23 %
23 %
ISO 4589-1/-2
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+12 ohm-cm
1.00e+12 ohm-cm
Conditioned; IEC 60093
1.00e+15 ohm-cm
1.00e+15 ohm-cm
IEC 60093
Surface Resistance 1.00e+13 ohm
1.00e+13 ohm
IEC 60093
Dielectric Constant 4.0

@Frequency 1.00e+6 Hz
4.0

@Frequency 1.00e+6 Hz
IEC 60250
4.3

@Frequency 100 Hz
4.3

@Frequency 100 Hz
IEC 60250
4.3

@Frequency 1.00e+6 Hz
4.3

@Frequency 1.00e+6 Hz
Conditioned; IEC 60250
7.0

@Frequency 100 Hz
7.0

@Frequency 100 Hz
Conditioned; IEC 60250
Dielectric Strength 31.0 kV/mm
787 kV/in
Conditioned; IEC 60243-1
34.0 kV/mm
864 kV/in
IEC 60243-1
Dissipation Factor 0.0080

@Frequency 100 Hz
0.0080

@Frequency 100 Hz
IEC 60250
0.017

@Frequency 1.00e+6 Hz
0.017

@Frequency 1.00e+6 Hz
IEC 60250
0.050

@Frequency 1.00e+6 Hz
0.050

@Frequency 1.00e+6 Hz
Conditioned; IEC 60250
0.13

@Frequency 100 Hz
0.13

@Frequency 100 Hz
Conditioned; IEC 60250
Comparative Tracking Index 475 V
475 V
IEC 60112
Descriptive Properties Value Comments
Additives Release agent
Features Heat stabilized or stable to heat
Form Pellets
ISO Shortname ISO 1874-PA 6,MHR,14-100,GF30
Processing Injection molding