Songhan Plastic Technology Co.,Ltd.
 POLYMER SEARCH

LG Chemical Lupox® TE5000LZ PBT+PC

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Unreinforced , Polyester, TP , Polybutylene Terephthalate (PBT)
Manufacturer LG Chemical
Trade Name Lupox®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LG Chemical Lupox® TE5000LZ PBT+PC.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Injection Molding, PBT+PC, High Impact, Dimensional Stability, Good WeatherabilityApplication: Automotive (Door Garnish)CAS No. 9003-01-04, 24968-12-5 and 103598-77-2Information provided by LG Chemical
Physical Properties Metric English Comments
Specific Gravity 1.22 g/cc
1.22 g/cc
ASTM D792
Water Absorption 0.080 %

@Temperature 23.0 °C,
Time 86400 sec
0.080 %

@Temperature 73.4 °F,
Time 24.0 hour
ASTM D570
Maximum Moisture Content 0.020
0.020
Injection Molding
Linear Mold Shrinkage, Flow 0.0070 - 0.010 cm/cm

@Thickness 3.20 mm
0.0070 - 0.010 in/in

@Thickness 0.126 in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength, Yield 55.9 MPa

@Thickness 3.20 mm
8110 psi

@Thickness 0.126 in
50mm/min; ASTM D638
Elongation at Break >= 100 %

@Thickness 3.20 mm
>= 100 %

@Thickness 0.126 in
50mm/min; ASTM D638
Flexural Yield Strength 83.4 MPa

@Thickness 6.40 mm
12100 psi

@Thickness 0.252 in
2.5mm/min; ASTM D790
Flexural Modulus 2.16 GPa

@Thickness 6.40 mm
313 ksi

@Thickness 0.252 in
2.5mm/min; ASTM D790
Izod Impact, Notched 5.88 J/cm

@Thickness 6.40 mm,
Temperature 23.0 °C
11.0 ft-lb/in

@Thickness 0.252 in,
Temperature 73.4 °F
ASTM D256
Thermal Properties Metric English Comments
Melting Point 225 °C
437 °F
@ Break; ASTM D3418
Deflection Temperature at 0.46 MPa (66 psi) 110 °C

@Thickness 6.40 mm
230 °F

@Thickness 0.252 in
Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 100 °C

@Thickness 6.40 mm
212 °F

@Thickness 0.252 in
Unannealed; ASTM D648
Processing Properties Metric English Comments
Rear Barrel Temperature 250 - 260 °C
482 - 500 °F
Injection Molding
Middle Barrel Temperature 250 - 260 °C
482 - 500 °F
Injection Molding
Front Barrel Temperature 255 - 265 °C
491 - 509 °F
Injection Molding
Nozzle Temperature 260 - 270 °C
500 - 518 °F
Injection Molding
Melt Temperature 260 - 270 °C
500 - 518 °F
Injection Molding
Mold Temperature 60.0 - 80.0 °C
140 - 176 °F
Injection Molding
Drying Temperature 120 °C
248 °F
Injection Molding
Dry Time 4.00 - 5.00 hour
4.00 - 5.00 hour
Injection Molding