LG Chemical LUSEP SP2306F SPS+GF30%, Flame Retardant
| Category | Polymer , Thermoplastic , Polystyrene (PS) , Syndiotactic Polystyrene (SPS) , Syndiotactic Polystyrene (SPS) with Glass or Carbon Fiber |
| Manufacturer | LG Chemical |
| Trade Name | LUSEP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical LUSEP SP2306F SPS+GF30%, Flame Retardant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Feature: Injection Molding, sPS+GF30%, Flame RetardantApplication: Pump Units, Pick-up Lends Holder, etcCAS No. 9003-53-6, 68928-70-1, 1309-64-4 and 65997-17-3Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.40 g/cc | 1.40 g/cc | ASTM D792 |
| Maximum Moisture Content | 0.020 | 0.020 | Injection Molding |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0090 cm/cm @Thickness 3.20 mm |
0.0030 - 0.0090 in/in @Thickness 0.126 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 113 MPa @Thickness 3.20 mm |
16400 psi @Thickness 0.126 in |
5mm/min; ASTM D638 |
| Elongation at Break | 2.0 % @Thickness 3.20 mm |
2.0 % @Thickness 0.126 in |
5mm/min; ASTM D638 |
| Flexural Yield Strength | 186 MPa @Thickness 3.20 mm |
27000 psi @Thickness 0.126 in |
1.3mm/min; ASTM D790 |
| Flexural Modulus | 9.32 GPa @Thickness 3.20 mm |
1350 ksi @Thickness 0.126 in |
1.3mm/min; ASTM D790 |
| Izod Impact, Notched | 0.686 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
1.29 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 260 °C @Thickness 6.40 mm |
500 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | >= 230 °C @Thickness 6.40 mm |
>= 446 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Strength | 31.0 kV/mm @Thickness 1.00 mm |
787 kV/in @Thickness 0.0394 in |
ASTM D149 |
| Comparative Tracking Index | 400 - 600 V | 400 - 600 V | Solution A; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 270 - 290 °C | 518 - 554 °F | Injection Molding |
| Middle Barrel Temperature | 280 - 310 °C | 536 - 590 °F | Injection Molding |
| Front Barrel Temperature | 290 - 310 °C | 554 - 590 °F | Injection Molding |
| Nozzle Temperature | 280 - 310 °C | 536 - 590 °F | Injection Molding |
| Melt Temperature | 280 - 310 °C | 536 - 590 °F | Injection Molding |
| Mold Temperature | 80.0 - 150 °C | 176 - 302 °F | Injection Molding |
| Drying Temperature | 80.0 - 100 °C | 176 - 212 °F | Injection Molding |
| Dry Time | 3.00 - 5.00 hour | 3.00 - 5.00 hour | Injection Molding |
| Screw Speed | 40 - 80 rpm | 40 - 80 rpm | Injection Molding |
Users viewing this material also viewed the following:
- Momentive Performance Materials Siloprenâ„¢ LSR 4630 FC Liquid Silicone Rubber - Healthcare
- SABIC Innovative Plastics SABIC PPCOMPOUND 37T1020 PP
- SABIC Innovative Plastics LNP Thermocomp 9X06477 SPS
- SK Chemicals SKYTHANE® S198A Polyester Based Thermoplastic Polyurethane Elastomer
- Arlon 55173R045 0.045" (1.14 mm) Cured Silicone Rubber with Fiberglass Substrate
- BASF Ultramid® 8260 HS PA6 (Dry)
- AK Steel CARLITE® M-3 Grain Oriented Electrical Steel (Extended Electro-Magnetic Data)
- Ineos Nova Zylar® 530 Clear Impact Modified Acrylic Copolymer (discontinued **)
- Kraton® D4150 K (O/E SBS) Linear Triblock Copolymer
- Axiall 1701 Clear 7002 Flexible PVC
Copyright © lookpolymers.com All Rights Reserved