Polymer Property : Flexural Modulus = 9.32 GPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Modulus	9.32 GPa	1350 ksi	ASTM D790
Mitsui AURUM® JGN6230 Thermoplastic Polyimide Resin, Amorphous (discontinued **) AURUM® is an easy melt, processable and recyclable thermoplastic polyimide resin that provides continuous service temperatures to 465° F in its amorphous state and up to 550° F when annealed to i..
Flexural Modulus	9.32 GPa @Temperature 150 °C	1350 ksi @Temperature 302 °F	ASTM D790
Mitsui AURUM® JGN6230 Thermoplastic Polyimide Resin, Crystalline (discontinued **) AURUM® is an easy melt, processable and recyclable thermoplastic polyimide resin that provides continuous service temperatures to 465° F in its amorphous state and up to 550° F when annealed to i..
Flexural Modulus	9.32 GPa @Thickness 3.20 mm	1350 ksi @Thickness 0.126 in	1.3mm/min; ASTM D790
LG Chemical LUMID GP2330B(W) PA66+GF33%, General Purpose Feature: Injection Molding, PA6+GF33%, General PurposeApplication: Automotive (Air Intake Manifold, Cylinder Head Cover)CAS No. 32131-17-2 and 65997-17-3Information provided by LG Chemical
Flexural Modulus	9.32 GPa @Thickness 3.20 mm	1350 ksi @Thickness 0.126 in	1.3mm/min; ASTM D790
LG Chemical LUMID GP2330BL PA66+GF33%, General Purpose Feature: Injection Molding, PA66+GF33%, General PurposeApplication: Automotive (Radiator Tank, Reservoir)Information provided by LG Chemical
Flexural Modulus	9.32 GPa	1350 ksi	DIN 53452; ASTM D790
Kolon KOPAÂ® KN333G33BL G/F Reinforced Nylon 66 KOPAÂ® is a thermoplastic resin with excellent mechanical, thermal and electrical properties and is widely used in the automobile, electrical and industrial parts.High tensile strength, outstandin..
Flexural Modulus	9.32 GPa @Thickness 3.20 mm	1350 ksi @Thickness 0.126 in	1.3mm/min; ASTM D790
LG Chemical LUSEP SP2306F SPS+GF30%, Flame Retardant Feature: Injection Molding, sPS+GF30%, Flame RetardantApplication: Pump Units, Pick-up Lends Holder, etcCAS No. 9003-53-6, 68928-70-1, 1309-64-4 and 65997-17-3Information provided by LG Chemical
Flexural Modulus	9.32 GPa	1350 ksi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics ULTEM SF2350 PEI Blend High flow Ultem blends for thin wall application
Flexural Modulus	9.32 GPa	1350 ksi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics ULTEM SF2350 PEI Blend (Asia Pacific) High flow Ultem blends for thin wall application
Flexural Modulus	9.32 GPa	1350 ksi	1.3 mm/min, 50 mm span; ASTM D 790
SABIC Innovative Plastics Ultem SF2350 PEI Blend (Europe-Africa-Middle East) High flow Ultem blends for thin wall applicationThis data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
Flexural Modulus	9.32 GPa	1350 ksi	2.8 mm/min; ASTM D790
Samsung Cheil Industries InfinoÂ® AR-5300H PBT/ASA, 30% Glass Filled Information provided by Samsung Cheil Industries.
Flexural Modulus	9.32 GPa	1350 ksi	2.8 mm/min; ASTM D790
Samsung Cheil Industries InfinoÂ® AR-9301 PA, Glass Filled General Purpose Information provided by Samsung Cheil Industries.
Flexural Modulus	9.32 GPa	1350 ksi	2.8 mm/min; ASTM D790
Samsung Cheil Industries InfinoÂ® EM-8240C MPPE, Glass Filled MPPE/GF material that is used in the main frame of banknote sortersInformation provided by Samsung Cheil Industries.
Flexural Modulus	9.32 GPa	1350 ksi	2.8 mm/min; ASTM D790
Samsung Cheil Industries InfinoÂ® AR-5300H PBT/ASA, 30% Glass Filled Information provided by Samsung Cheil Industries.
Flexural Modulus	9.32 GPa	1350 ksi	2.8 mm/min; ASTM D790
Samsung Cheil Industries InfinoÂ® AR-9301 PA, Glass Filled General Purpose Information provided by Samsung Cheil Industries.
Flexural Modulus	9.32 GPa	1350 ksi	2.8 mm/min; ASTM D790
Samsung Cheil Industries InfinoÂ® EM-8240C MPPE, Glass Filled MPPE/GF material that is used in the main frame of banknote sortersInformation provided by Samsung Cheil Industries.
Flexural Modulus	9.32 GPa	1350 ksi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP RF007ES PA 66 LNP* THERMOCOMP* RF007ES is a compound based on Nylon 66 resin containing 35% Glass Fiber. Added features of this material include: Heat Stabilized, Easy Molding.
Flexural Modulus	9.32 GPa	1350 ksi	ASTM D790
Shinkong Synthetic Fibers ShiniteÂ® D202G30 PBT, 30% Glass Filled, Fire Retardant Information from Shinkong Synthetic Fibers Corp.
Flexural Modulus	9.32 GPa	1350 ksi	ASTM D790
Shinkong Synthetic Fibers ShiniteÂ® D202G30 PBT, 30% Glass Filled, Fire Retardant Information from Shinkong Synthetic Fibers Corp.
Flexural Modulus	9.32 - 17.0 GPa	1350 - 2470 ksi	Average value: 13.3 GPa Grade Count:18
Overview of materials for Polyethylene Terephthalate (PET), 50% Glass Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polyethylene Terephthalate (PET), 50% Glass Reinforced". Specific grades with glass content between 45% ..
Flexural Modulus	9.32 GPa	1350 ksi	ASTM D790
Samyang Tripet® 2500G45 Polyethylene Terephthalate, 45% Glass Fiber Reinforced TRIPET® has excellent heat resistance, good surface, chemical resistance and high electrical performance.Applications:Coil BobbinConnectorMotor HousingLamp HousingRelay BaseIron bodyAll information..