Huntsman PE1059 Film Extrusion Polyethylene  (discontinued **)

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Film Grade
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Huntsman PE1059 Film Extrusion Polyethylene  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Homopolymer and FDA compliant.Features: Excellent draw down and good processability.Applications: Film extrusion: non-abrasive packaging applications.FDA Notes: Conforms to FDA regulation 21 CFR 177.1520 (c)2.2 under condition of use B through H described in Table 2 of 21 CFR 176.170Film properties based on 1.0 guage (25 µm) thickness; blow-up ratio 2:1.Information provided by Huntsman Corporation
Physical Properties Metric English Comments
Density 0.922 g/cc
0.0333 lb/in³
ASTM D1505
Thickness 25.4 microns
1.00 mil
Melt Flow 6.5 g/10 min
6.5 g/10 min
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Shore D 48
48
ASTM D2240
Tensile Strength, Ultimate 11.0 MPa
1600 psi
ASTM D638
Tensile Strength, Yield 11.0 MPa
1600 psi
ASTM D638
Film Elongation at Break, MD 320 %
320 %
ASTM D882
Film Elongation at Break, TD 380 %
380 %
ASTM D882
Elongation at Break 400 %
400 %
ASTM D638
Modulus of Elasticity 0.297 GPa
43.1 ksi
Secant; ASTM D638
Secant Modulus, MD 0.204 GPa
29.6 ksi
ASTM D882
Secant Modulus, TD 0.255 GPa
37.0 ksi
ASTM D882
Dart Drop 1.97 g/micron
50.0 g/mil
ASTM D1709
Dart Drop Test 50.0 g
0.110 lb
ASTM D1709
Film Tensile Strength at Break, MD 20.0 MPa
2900 psi
ASTM D882
Film Tensile Strength at Break, TD 15.0 MPa
2180 psi
ASTM D882
Thermal Properties Metric English Comments
Vicat Softening Point 92.0 °C
198 °F
ASTM D1525
Optical Properties Metric English Comments
Gloss 42 %
42 %
at 45°; ASTM D523
Processing Properties Metric English Comments
Melt Temperature 160 - 171 °C
320 - 340 °F