Physical Properties | Metric | English | Comments |
---|---|---|---|
Melt Flow | 6.5 g/10 min @Load 21.6 kg, Temperature 190 °C |
6.5 g/10 min @Load 47.6 lb, Temperature 374 °F |
without Catalyst MB addition; Internal Method |
Solvay Specialty Polymers Cogegum® GFR/360 Polyolefin, Unspecified
(Unverified Data**) Cogegum® XLPO-HFFR - Crosslinkable Halogen Free Fire Retardant compound Silane grafted compound moisture curable by addition of a catalyst masterbatch (Sioplas® method). It consists of a polyolefi.. |
|||
Melt Flow | 6.5 g/10 min @Load 3.80 kg, Temperature 230 °C |
6.5 g/10 min @Load 8.38 lb, Temperature 446 °F |
|
Polycasa Acryl® KR 2015/1 Acrylic, Impact Grade Medium-impact grade with very good flow behavior, especially mechanically stressed parts with long flow paths; e.g. strip light diffusers. Can be extruded into thin tubes, sheet and film.Data was c.. |
|||
Melt Flow | 6.5 g/10 min | 6.5 g/10 min | Condition G |
Ineos Nova 1511 High Heat Crystal Polystyrene
(discontinued **) High flow and high heat resistance, Excellent clarity, USP Class VIApplications: Injection moldingExposure to gamma radiation in the 2.02-6.06 megarad range has no significant effect on the physical.. |
|||
Melt Flow | 6.5 g/10 min @Load 2.16 kg, Temperature 190 °C |
6.5 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
Chevron Phillips HiD® 9706 HDPE Injection Molding Resin
(discontinued **) Resin Type: linear homopolymerCharacteristics: moderate flow, good impact strength, excellent stiffness, good ESCR, moderate shrinkage resistanceApplications: crates and totes, structural foamInform.. |
|||
Melt Flow | 6.5 g/10 min @Load 2.16 kg, Temperature 343 °C |
6.5 g/10 min @Load 4.76 lb, Temperature 649 °F |
ASTM D1238 |
Solvay Specialty Polymers Udel® GF-130 Polysulfone (PSU)
(Unverified Data**) Udel GF-130, resin is a 30% glass fiber reinforced polysulfone compound. Glass fiber substantially increases the rigidity, tensile strength, creep resistance, dimensional stability and chemical resi.. |
|||
Melt Flow | 6.5 g/10 min @Load 2.16 kg, Temperature 343 °C |
6.5 g/10 min @Load 4.76 lb, Temperature 649 °F |
ASTM D1238 |
Solvay Specialty Polymers Udel® P-1700 LCD Polysulfone (PSU)
(Unverified Data**) Udel P-1700 LCD polysulfone is especially well suited for the fabrication of porous membranes for filtration applications. The membranes are usually in the form of hollow fibers, but tube, plate or .. |
|||
Melt Flow | 6.5 g/10 min @Load 2.16 kg, Temperature 343 °C |
6.5 g/10 min @Load 4.76 lb, Temperature 649 °F |
ASTM D1238 |
Solvay Specialty Polymers Udel® P-1800 Polysulfone (PSU)
(discontinued **) Udel P-1800 is a powdered grade of polysulfone with molecular weight similar to that of Udel P-1700 polysulfone. It is well suited for the fabrication of porous membranes that can be made into hollo.. |
|||
Melt Flow | 6.5 g/10 min @Load 2.16 kg, Temperature 230 °C |
6.5 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
LyondellBasell Pro-fax SA861 Polypropylene Random Copolymer, Cast Film Extrusion Key Features: polypropylene random copolymer resin formulated for cast film extrusion, good optical properties, excellent slip properties, FDA acceptable, improved cold temperature impact resistance.. |
|||
Melt Flow | 6.5 g/10 min | 6.5 g/10 min | ASTM D1238 |
LyondellBasell Petrothene® NA336149 Low Density Polyethylene ApplicationsPETROTHENE NA 336 is a homopolymer resin specifically engineered for garment film and dry cleaning bag applications. This resin is also suitable for any application requiring thin gauge.. |
|||
Melt Flow | 6.5 g/10 min | 6.5 g/10 min | ASTM D1238 |
LyondellBasell Plexar® PX5125 Extrudable Tie-Layer Resin - Anhydride Modified LLDPE ApplicationsPLEXAR tie-layers are chemically modified resins used to bond unlike materials, primarily in packaging and industrial applications. Common adherents include polyethylene resins and copo.. |
|||
Melt Flow | 6.5 g/10 min | 6.5 g/10 min | Condition G |
Ineos Nova 1510 High Heat Crystal Polystyrene High flow and high heat resistance, Excellent clarity, USP Class VIApplications: Injection moldingExposure to gamma radiation in the 2.02-6.06 megarad range has no significant effect on the physical.. |
|||
Melt Flow | 6.5 g/10 min @Load 21.6 kg, Temperature 190 °C |
6.5 g/10 min @Load 47.6 lb, Temperature 374 °F |
ISO 1133 |
Iran Petrochemical (PCC) HB4265 High Density Polyethylene HB4265 is a high molecular weight high density polyethylene.Applications: tanks, industrial, blow molding.Information provided by Iran Petrochemical Commercial Co. |
|||
Melt Flow | 6.5 g/10 min | 6.5 g/10 min | ASTM D1238 |
KKPC Kuhmo HI 425TVD High Flow/High Heat Resistant HIPS Key features: High-impact-fluidity. Common Uses: TV cover, computer case.HIPS is a functional resin made by copolymerization of styrene monomer and PBR. It shows excellent balance between impact-res.. |
|||
Melt Flow | 6.5 g/10 min @Load 2.16 kg, Temperature 190 °C |
6.5 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
Techmer ES HiFill FR® HDPE 8904 FR UV GY Availability: North AmericaForms: PelletsAdditive: UV StabilizerFeatures: Flame Retardant and Good UV ResistanceAppearance: GrayInformation provided by TP Composites, Inc. |
|||
Melt Flow | 6.5 g/10 min @Load 2.16 kg, Temperature 343 °C |
6.5 g/10 min @Load 4.76 lb, Temperature 649 °F |
ASTM D1238 |
Solvay Specialty Polymers Udel® P-1700 Polysulfone (PSU) Udel® P-1700 polysulfone (PSU) is a tough, rigid, high-strength thermoplastics suitable for continuous use up to 300°F (149°C). It is resistant to oxidation and hydrolysis and withstand pro.. |
|||
Melt Flow | 6.5 g/10 min @Load 3.80 kg, Temperature 230 °C |
6.5 g/10 min @Load 8.38 lb, Temperature 446 °F |
ISO 1133 |
Styron TYRILâ„¢ 875 SAN Resin Overview: TYRIL Styrene-actylonitrile (SAN) resins are designed by Styron to offer superior chemical resistance, strength, hardness and dimensional stability in a broad range of product applications.. |
|||
Melt Flow | 6.5 g/10 min @Load 2.16 kg, Temperature 230 °C |
6.5 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
Borealis Borseal™ TD110BF Terpolymer for BOPP Film Borseal TD110BF is a C2/C4 terapolymer film resin.Borseal TD110BF is especially developed for use as sealing layers in coextruded BOPP film (manufactured on Stenter frame and double bubble film proc.. |
|||
Melt Flow | 6.5 g/10 min @Load 2.16 kg, Temperature 230 °C |
6.5 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
Borealis Borseal™ TD115BF Terpolymer for BOPP Film Borseal TD115BF is a C2/C4 terapolymer film resin.Borseal TD115BF is especially developed for use as sealing layers in coextruded BOPP film (manufactured on Stenter frame and double bubble film proc.. |
|||
Melt Flow | 6.5 g/10 min @Load 2.16 kg, Temperature 190 °C |
6.5 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
A. Schulman POLYBATCH™ White P8555 SD Concentrate Based In Homopolymer Polypropylene DescriptionPOLYBATCH® P8555 SD is a white masterbatch containing 50% TiO2 based in homopolymer polypropylene. This product offers excellent dispersion and a very low moisture content which permits.. |
|||
Melt Flow | 6.5 g/10 min @Load 5.00 kg, Temperature 200 °C |
6.5 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
Videolar 825 High Impact Polystyrene (HIPS) Injection molding gradeMedium melt flow and high glossGood balance between rigidity and impactFeatures: Excellent mechanical strengthExcellent temperature resistancehigh impactApplications: Toys, ap.. |
|||
Melt Flow | 6.5 g/10 min | 6.5 g/10 min | Cond. E; ASTM D1238 |
DuPont Conpol™ 20B Ethylene-Methacrylic Acid Additive Resin Conpol™ additive resins, supplied in pellet form, are designed to modify the surface properties of films or coatings of Surlyn® ionomer resins and Nucrel® acid copolymer resins. They are concentr.. |
|||
Melt Flow | 6.5 g/10 min @Load 1.20 kg, Temperature 300 °C |
6.5 g/10 min @Load 2.65 lb, Temperature 572 °F |
ISO 1133 |
Covestro Makrolon® 3100 Polycarbonate Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• General purpose• Hig.. |
|||
Melt Flow | 6.5 g/10 min @Load 1.20 kg, Temperature 300 °C |
6.5 g/10 min @Load 2.65 lb, Temperature 572 °F |
ISO 1133 |
Covestro Makrolon® 3107 MAS167 Polycarbonate Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• General purpose• Hig.. |
|||
Melt Flow | 6.5 g/10 min @Load 1.20 kg, Temperature 300 °C |
6.5 g/10 min @Load 2.65 lb, Temperature 572 °F |
ISO 1133 |
Covestro Makrolon® 3158 Polycarbonate Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• Medical devices - bioc.. |
|||
Melt Flow | 6.5 g/10 min @Load 2.16 kg, Temperature 190 °C |
6.5 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
ExxonMobil LDPE LGA 105 Low Density Polyethylene Resin Product Description: LGA 105 is a homopolymer, garment film resin with good toughness. It is capable of being draw-down to thin gauges.Availability: North America Additive: Antiblock: NoSlip: NoPro.. |
|||
Melt Flow | 6.5 g/10 min @Load 2.16 kg, Temperature 190 °C |
6.5 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
DuPont Performance Polymers Hytrel® G4078LS NC010 Polyester Elastomer TPC-ET
(Unverified Data**) 40 Shore D Standard Performance Polyester Elastomer with Light ProtectionInformation provided by DuPont Performance Polymers |
|||
Melt Flow | 6.5 g/10 min @Load 1.60 kg, Temperature 250 °C |
6.5 g/10 min @Load 3.53 lb, Temperature 482 °F |
Calculated from Volume Flow Rate of 5 cm<sup>3</sup>/10min.; ISO 1133 |
DSM Arnite® T06 200 SNF PBT (European Grade) Arnite resins are engineered to provide specific performance in applications where DSM technology can offer value.Arnite Molding resins: Standard Unfilled and Reinforced materialsHigh modulus Flame .. |
|||
Melt Flow | 6.5 g/10 min @Load 5.00 kg, Temperature 200 °C |
6.5 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
M. Holland Company IS330 Polystyrene, High Impact
(discontinued **) Features: Impact ModifiedUses: Audio Tapes, Household Goods, ToysApprovals: FDA 21 CFR 177.1640Processing Method: Injection MoldingInformation provided by M. Holland. |
|||
Melt Flow | 6.5 g/10 min @Load 2.16 kg, Temperature 190 °C |
6.5 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
A. Schulman POLYBATCH™ White P8555 SD Concentrate Based In Homopolymer Polypropylene DescriptionPOLYBATCH® P8555 SD is a white masterbatch containing 50% TiO2 based in homopolymer polypropylene. This product offers excellent dispersion and a very low moisture content which permits.. |