Hexcel® HexPly® F650 Bismaleimide Resin with T300 Fiber

Category Polymer , Thermoset , Polyimide, TS
Manufacturer Hexcel
Trade Name HexPly®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Hexcel® HexPly® F650 Bismaleimide Resin with T300 Fiber.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Thermal Aging at 232°C; Composition T300 Fiber, 6K, UD Tape - 148 g/m2; Laminate Physicals: 32.7% Resin content, 60.0% Fiber volumeInformation provided by HexCel
Mechanical Properties Metric English Comments
Flexural Yield Strength 1124 MPa

@Temperature 232 °C
 163000 psi

@Temperature 450 °F
 Control (Prepreg with no freezer or out time exposure)
1151 MPa

@Temperature 232 °C
 166900 psi

@Temperature 450 °F
 1608 Hrs
1427 MPa

@Temperature 232 °C
 207000 psi

@Temperature 450 °F
 424 Hrs
1427 MPa

@Temperature 232 °C
 207000 psi

@Temperature 450 °F
 804 Hrs
1482 MPa

@Temperature 232 °C
 214900 psi

@Temperature 450 °F
 1255 Hrs
1489 MPa

@Temperature 23.0 °C
 216000 psi

@Temperature 73.4 °F
 1608 Hrs
1538 MPa

@Temperature 232 °C
 223100 psi

@Temperature 450 °F
 2010 Hrs
1606 MPa

@Temperature 23.0 °C
 232900 psi

@Temperature 73.4 °F
1737 MPa

@Temperature 23.0 °C
 251900 psi

@Temperature 73.4 °F
 1255 Hrs
1744 MPa

@Temperature 23.0 °C
 252900 psi

@Temperature 73.4 °F
 424 Hrs, Room temperature
1793 MPa

@Temperature 23.0 °C
 260100 psi

@Temperature 73.4 °F
 2010 Hrs
1827 MPa

@Temperature 23.0 °C
 265000 psi

@Temperature 73.4 °F
 804 Hrs
Flexural Modulus 121 GPa

@Temperature 232 °C
 17500 ksi

@Temperature 450 °F
 Control (Prepreg with no freezer or out time exposure)
123 GPa

@Temperature 232 °C
 17800 ksi

@Temperature 450 °F
 1255 Hrs
123 GPa

@Temperature 232 °C
 17800 ksi

@Temperature 450 °F
 1608 Hrs
123 GPa

@Temperature 23.0 °C
 17800 ksi

@Temperature 73.4 °F
125 GPa

@Temperature 232 °C
 18100 ksi

@Temperature 450 °F
 804 Hrs
126 GPa

@Temperature 232 °C
 18300 ksi

@Temperature 450 °F
 424 Hrs
126 GPa

@Temperature 23.0 °C
 18300 ksi

@Temperature 73.4 °F
 1608 Hrs
126 GPa

@Temperature 23.0 °C
 18300 ksi

@Temperature 73.4 °F
 2010 Hrs
128 GPa

@Temperature 23.0 °C
 18600 ksi

@Temperature 73.4 °F
 1255 Hrs
130 GPa

@Temperature 23.0 °C
 18900 ksi

@Temperature 73.4 °F
 804 Hrs
132 GPa

@Temperature 23.0 °C
 19100 ksi

@Temperature 73.4 °F
 424 Hrs
145 GPa

@Temperature 232 °C
 21000 ksi

@Temperature 450 °F
 2010 Hrs
Shear Strength 52.0 MPa

@Temperature 232 °C
 7540 psi

@Temperature 450 °F
 Short Beam; Control (Prepreg with no freezer or out time exposure)
66.0 MPa

@Temperature 232 °C
 9570 psi

@Temperature 450 °F
 Short Beam; 1255 Hrs
68.9 MPa

@Temperature 232 °C
 9990 psi

@Temperature 450 °F
 Short Beam; 804 Hrs
71.7 MPa

@Temperature 232 °C
 10400 psi

@Temperature 450 °F
 Short Beam; 424 Hrs
76.5 MPa

@Temperature 232 °C
 11100 psi

@Temperature 450 °F
 Short Beam; 1608 Hrs
76.5 MPa

@Temperature 232 °C
 11100 psi

@Temperature 450 °F
 Short Beam; 2010 Hrs
101 MPa

@Temperature 23.0 °C
 14600 psi

@Temperature 73.4 °F
101 MPa

@Temperature 23.0 °C
 14600 psi

@Temperature 73.4 °F
103 MPa

@Temperature 23.0 °C
 14900 psi

@Temperature 73.4 °F
110 MPa

@Temperature 23.0 °C
 16000 psi

@Temperature 73.4 °F
111 MPa

@Temperature 23.0 °C
 16100 psi

@Temperature 73.4 °F
112 MPa

@Temperature 23.0 °C
 16200 psi

@Temperature 73.4 °F