Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Shear Strength 103 MPa

@Temperature 82.2 °C
14900 psi

@Temperature 180 °F
Beam, V-Notched; Dry; Autoclave Cured; ASTM D5379-93
Park Electrochemical Nelcote® E-765 Epoxy Prepreg, T300 6K 5HS Reinforced
Nelcote® E-765 is a tough 250°F cure prepreg system designed to replace 350°F cure systems in aircraft structural applications. FAA-approved Design Allowable Databases are available upon request...
Shear Strength 103 MPa

@Temperature 399 °C
15000 psi

@Temperature 750 °F
18-8 Stainless Steel butt joint
Lucas-Milhaupt BRAZE 541 Silver Based Cadmium Free Filler Metal
Characteristics:Braze 541 is an intermediate temperature silver brazing alloy with a rather long, 235EF (130EC) melting range. It has a tendency to liquate (i.e. separate into low and high melting ..
Shear Strength 103 MPa

@Temperature 23.0 °C
14900 psi

@Temperature 73.4 °F
Hexcel® HexPly® F650 Bismaleimide Resin with T300 Fiber
Thermal Aging at 232°C; Composition T300 Fiber, 6K, UD Tape - 148 g/m2; Laminate Physicals: 32.7% Resin content, 60.0% Fiber volumeInformation provided by HexCel
Shear Strength 103 MPa

@Temperature 23.0 °C
14900 psi

@Temperature 73.4 °F
ILSS; prEN2563
Hexcel® HexPly® M48 180°C/356°F Curing Epoxy Matrix, M48/35%/150/AS7 GS
Fiber: AS7 GS, UD, 150 g/m2Information provided by HexCel
Shear Strength 103 MPa

@Temperature 23.0 °C
14900 psi

@Temperature 73.4 °F
Hexcel® HexPly® M65 Bismaleimide Resin, Carbon Fabric Form
Fibers: T300-3K, AS4C-3KInformation provided by HexCel