- ExxonMobil Exceed™ 357C32 LDPE/Hexene Premium Cast Stretch Film Resin (discontinued **)
ExxonMobil Exceed™ 357C32 LDPE/Hexene Premium Cast Stretch Film Resin (discontinued **)
| Category | Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Film Grade |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | ExxonMobil Exceed™ 357C32 LDPE/Hexene Premium Cast Stretch Film Resin
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by the manufacturer, Exxon Chemical.A hexene copolymer produced using Exxon Chemical's EXXPOL® technology. Films made from EXCEED 357C32 resin have outstanding tensile properties and impact and puncture toughness.Applications: Cast stretch film. Data for film properties below based on 0.8 mil film.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.917 g/cc | 0.0331 lb/in³ | Exxon Method |
| Thickness | 20.3 microns | 0.800 mil | |
| Melt Flow | 3.4 g/10 min | 3.4 g/10 min | Exxon Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | 7.10 MPa | 1030 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 7.10 MPa | 1030 psi | ASTM D882 |
| Film Elongation at Break, MD | 420 % | 420 % | ASTM D882 |
| Film Elongation at Break, TD | 650 % | 650 % | ASTM D882 |
| Secant Modulus, MD | 0.113 GPa | 16.4 ksi | ASTM D882 |
| Secant Modulus, TD | 0.137 GPa | 19.9 ksi | ASTM D882 |
| Elmendorf Tear Strength MD | 160 g | 160 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 450 g | 450 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 7.87 g/micron | 200 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 22.2 g/micron | 563 g/mil | ASTM D1922 |
| Dart Drop | 11.3 g/micron | 288 g/mil | F50; ASTM D1709 |
| Dart Drop Test | 230 g | 0.507 lb | F50; ASTM D-1709 |
| Film Tensile Strength at Break, MD | 68.0 MPa | 9860 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 48.0 MPa | 6960 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 115 °C | 239 °F | Exxon Method |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 1.5 % | 1.5 % | ASTM D1003 |
| Gloss | 97 % | 97 % | 45°, ASTM D-2457 |