- Polymer Property : Melt Flow = 3.4 g/10 min
Polymer Property : Melt Flow = 3.4 g/10 min Product List
Physical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Flow | 3.4 g/10 min @Load 2.16 kg, Temperature 190 °C |
3.4 g/10 min @Load 4.76 lb, Temperature 374 °F |
Procedure A; ASTM D1238 |
| PolyOne Syncure™ V0044G RoHS Natural Polyethylene, Crosslinked (XLPE) Available as Flame Retardant Catalyst Masterbatch component for PolyOne Syncure System.Dispersion measured on a 100 phr S1025A / 90 phr V0044G Syncure System. Cured for 6 hours in water at 90°C. Di.. |
|||
| Melt Flow | 3.4 g/10 min @Load 2.16 kg, Temperature 190 °C |
3.4 g/10 min @Load 4.76 lb, Temperature 374 °F |
Procedure A; ASTM D1238 |
| PolyOne Syncure™ V0044G-UV RoHS Natural Polyethylene, Crosslinked (XLPE) Available as Flame Retardant Catalyst Masterbatch component for PolyOne Syncure System S110FV-UV.Information provided by PolyOne |
|||
| Melt Flow | 3.4 g/10 min @Load 1.00 kg, Temperature 235 °C |
3.4 g/10 min @Load 2.20 lb, Temperature 455 °F |
Procedure A Condition Q; ASTM D1238 |
| Network Polymers Softflex® 3300 Description: Softflex® Thermoplastic Elastomer AlloyInformation provided by Network Polymers Inc. |
|||
| Melt Flow | 3.4 - 4.2 g/10 min @Load 2.16 kg, Temperature 230 °C |
3.4 - 4.2 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238/L |
| NIZHNEKAMSKNEFTEKHIM PP 2641J (T31SE) Propylene Homopolymer Product obtained by polymerization of propylene in presence of complex metalorganic catalysts. It incorporates increased long-term thermal stability, thermal-oxidative degradation resistance when P.. |
|||
| Melt Flow | 3.4 g/10 min | 3.4 g/10 min | Condition G |
| Ineos Nova 2110 General Purpose Crystal Polystyrene
(discontinued **) Moderately high heat resistance, Good balance of strength and ease of processing, USP Class VIApplications: Foam extrusion, Biaxially oriented sheet, Thermoformed drinkware, Molded packagingExposure.. |
|||
| Melt Flow | 3.4 g/10 min | 3.4 g/10 min | Exxon Method |
| ExxonMobil Exceed™ 357C32 LDPE/Hexene Premium Cast Stretch Film Resin
(discontinued **) Data provided by the manufacturer, Exxon Chemical.A hexene copolymer produced using Exxon Chemical's EXXPOL® technology. Films made from EXCEED 357C32 resin have outstanding tensile properties and.. |
|||
| Melt Flow | 3.4 g/10 min @Load 2.16 kg, Temperature 230 °C |
3.4 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Phillips 66 COPYLENE® CH034 Polypropylene, Homopolymer, BOPP COPYLENE™ CH034, a polypropylene homopolymer resin, is designed for the production of biaxially oriented polypropylene films (BOPP). Potential uses include metalized film applications, (either dire.. |
|||
| Melt Flow | 3.4 g/10 min @Load 2.16 kg, Temperature 230 °C |
3.4 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Phillips 66 COPYLENE® CH034EW Polypropylene, Homopolymer, Slit Film, LWCO COPYLENE™ CH034EW is a medium flow polypropylene homopolymer resin suitable for general injection molding or extrusion applications. Applications: Raffia/tapes/strapping. Equivalent to Pro-fax® HL.. |
|||
| Melt Flow | 3.4 g/10 min | 3.4 g/10 min | ASTM D1238 |
| I. Stern PS2110 General Purpose Crystal Polystyrene Features:Moderately High Heat ResistanceUL Classification 94 HBExcellent Water ClarityApplicationsDisplaysHouse waresInformation provided by I. Stern & Co. Inc. |
|||
| Melt Flow | 3.4 g/10 min @Load 2.16 kg, Temperature 230 °C |
3.4 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Ineos H03G-05 Polypropylene Homopolymer Grade H03G-05 is a polypropylene homopolymer designed for BOPP applications and meet the requirements of the U.S. Food and Drug administration as specified in 12 CFR 177.1520.Applications:Food Packa.. |
|||
| Melt Flow | 3.4 g/10 min @Load 5.00 kg, Temperature 200 °C |
3.4 g/10 min @Load 11.0 lb, Temperature 392 °F |
ISO 1133 |
| Styrolution PS 165 N/L GPPS Styrolution PS 165N/L is a high molecular weight, good flowing grade, often blended with high impact extrusion grades.High molecular weightGood flow characteristicsAppropriate for blending with HIPS.. |
|||
| Melt Flow | 3.4 g/10 min @Load 5.00 kg, Temperature 200 °C |
3.4 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D 1238 |
| Styrolution PS 2600/2601 GPPS Foam extrusionLow residual styrene monomer contentModerate heat resistanceGood balance of strength and ease of processingUSP Class VI certifiedUL Classification 94 HBInformation provided by Styrolut.. |
|||
| Melt Flow | 3.4 g/10 min @Load 5.00 kg, Temperature 200 °C |
3.4 g/10 min @Load 11.0 lb, Temperature 392 °F |
ISO 1133 |
| Styrolution PS ESCRimo HIPS Styrolution PS ESCRimo is a high impact polystyrene grade with an improved stress cracking resistance compared to conventional high impact polystyreneHigh ESCR resistanceDeep draw thermoformingUL 94.. |
|||
| Melt Flow | 3.4 g/10 min @Temperature 230 °C |
3.4 g/10 min @Temperature 446 °F |
ASTM D1238 |
| Dow 5D98 Polypropylene Resin DOW 5D98 is intended for use in oriented polypropylene (OPP) film processes.Information provided by DowDow Announced Sale of Global Polypropylene Business to Braskem in July 2011. |
|||
| Melt Flow | 3.4 g/10 min @Load 2.16 kg, Temperature 190 °C |
3.4 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| BASF Ultraform® N2320 006 POM Description: Is a POM, high-molecular-weight grade with somewhat increased flowability for injection molding of relatively thick-walled moldings.Information provided by BASF |
|||
| Melt Flow | 3.4 g/10 min @Load 2.16 kg, Temperature 230 °C |
3.4 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Phillips 66 COPYLENE® CH034EV Polypropylene, Homopolymer, Fiber, Tape, UV COPYLENE™ CH034EV is a polypropylene homopolymer resin designed for fiber applications. Applications: Filament Yarn, Geotextile & agriculture. Equivalent to Pro-fax® HL348JInformation provided by .. |
|||
| Melt Flow | 3.4 g/10 min @Load 2.16 kg, Temperature 230 °C |
3.4 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Phillips 66 COPYLENE® CH034W Polypropylene, Homopolymer, Slit Film, LWCO COPYLENE™ CH034W is a medium flow polypropylene homopolymer resin suitable for general injection molding or extrusion applications. Applications: Housewares, Raffia/tapes/strapping. Equivalent to P.. |
|||
| Melt Flow | 3.4 g/10 min @Load 2.16 kg, Temperature 230 °C |
3.4 g/10 min @Load 4.76 lb, Temperature 446 °F |
|
| BASF Novolen® 1102 J Polypropylene Data was collected by ISO methods and provided by BASF. |
|||
| Melt Flow | 3.4 g/10 min @Load 2.16 kg, Temperature 230 °C |
3.4 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Ineos H03G-01 Polypropylene Homopolymer This is a homopolymer designed for tenter frame BOPP processing and meets the requirements of the U.S. Food and Drug Administration as specified in 21 CFR 177.1520.ApplicationsFood packagingOverwrap.. |
|||
| Melt Flow | 3.4 g/10 min @Load 2.16 kg, Temperature 190 °C |
3.4 g/10 min @Load 4.76 lb, Temperature 374 °F |
Procedure A; ASTM D1238 |
| PolyOne Syncure™ V0044G S-1 RoHS Natural Polyethylene, Crosslinked (XLPE) Available as Flame Retardant Catalyst Masterbatch component for PolyOne Syncure System.Information provided by PolyOne |
|||