Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Film Tensile Strength at Break, TD | 48.0 MPa | 6960 psi | ISO 527-3 |
Polimeri Europa Eraclene® FA 706 Hexene Copolymer High Density Polyethylene - Blown Film Extrusion Eraclene FA 706 is a high density polyethylene resin (HDPE), hexene copolymer, with antioxidants, suitable for blown film extrusion.Films manufactured with Eraclene FA 706 show good processability t.. |
|||
Film Tensile Strength at Break, TD | 48.0 MPa | 6960 psi | ASTM D 882 |
NOVA Chemicals Sclair® FP019-C Octene Copolymer LLDPE Film Resin FP019-C is biologically and chemically inert.Features: Superior toughness, Outstanding melt strength, Excellent sealability, Low gelAdditives: Polymer Process AidApplications: High toughness film,.. |
|||
Film Tensile Strength at Break, TD | 48.0 MPa | 6960 psi | ASTM D 882 |
NOVA Chemicals Sclair® FP019-D Octene Copolymer LLDPE Film Resin FP019-D is biologically and chemically inert.Features: Superior toughness, Outstanding melt strength, Excellent sealability, Low gelAdditives: Slip, Antiblock, Polymer Process AidApplications: Hig.. |
|||
Film Tensile Strength at Break, TD | 48.0 MPa | 6960 psi | ASTM D882 |
Eastman 9921P PET Film
(discontinued **) Voridian PET 9921P is produced at Voridian’s manufacturing sites in Rotterdam and Zarate, it is PTA/CHDM based, and it is sold to customers in the Europe, Middle East and Africa, Argentina, Bolivia.. |
|||
Film Tensile Strength at Break, TD | 48.0 MPa | 6960 psi | ASTM D882 |
ExxonMobil Exceed™ 357C32 LDPE/Hexene Premium Cast Stretch Film Resin
(discontinued **) Data provided by the manufacturer, Exxon Chemical.A hexene copolymer produced using Exxon Chemical's EXXPOL® technology. Films made from EXCEED 357C32 resin have outstanding tensile properties and.. |
|||
Film Tensile Strength at Break, TD | 48.0 MPa | 6960 psi | ASTM D882 |
Braskem HM 150 HDPE Monofilament Polyethylene
(discontinued **) Applications: Raschel; flat yarn; general and industrial rape netting. Information provided by Braskem |
|||
Film Tensile Strength at Break, TD | 48.0 MPa | 6960 psi | ASTM D882 |
DuPont™ Dartek® N-201 Nylon 6,6 Non-Forming Film, 25 µm Thickness
(discontinued **) Data provided by DuPont Packaging Polymers.A nylon film made from type 6,6 polymer - the condensation product of adipic acid and hexamethylene diamine. Primarily formulated for pouch and primal bag .. |
|||
Film Tensile Strength at Break, TD | 48.0 MPa | 6960 psi | ISO 1184 |
SIDPEC EGYPTENE® HD 4602 FA HDPE Film Applications:Strong filmTrash bagShopping bagFilm properties were measured on 15 micron film extruded at a blow up ratio of 5:1, 8D neck height.Information provided by Interchim s.r.l., official dis.. |
|||
Film Tensile Strength at Break, TD | 48.0 MPa | 6960 psi | ISO 527-3 |
Borealis Borstar® FB1350 Medium Density Polyethylene Borstar® FB1350 is a linear medium density polyethylene grade combining excellent extrusion properties with high film stiffness. Borstar® FB1350 is well suited for mono- and coextrusion of films .. |
|||
Film Tensile Strength at Break, TD | 48.0 MPa | 6960 psi | ASTM D882 |
Eastman Cadence™ GS5 Clear (Unpigmented) Copolyester for film calendering Eastman Cadence™ copolyester, for calendered films, is a specialty plastic developed to meet the demand for an environmentally responsible material for the calendering industry. Available in diffe.. |
|||
Film Tensile Strength at Break, TD | 48.0 MPa | 6960 psi | ISO 527-3 |
Total Lumicene® mPE M 2710 EP Metallocene Polyethylene, Blown Film Lumicene® mPE M 2710 EP is a second generation metallocene based Low Density Polyethylene with hexene as comonomer.Lumicene® mPE M 2710 EP can be processed at high output rates with low extrusion .. |