DuPont Performance Polymers Hytrel® 4053FG NC010 Polyester Elastomer TPC-ET  (Unverified Data**)

Category Polymer , Thermoplastic , Polyester, TP , Polyester Thermoplastic Elastomer
Manufacturer DuPont Performance Polymers
Trade Name Hytrel®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Hytrel® 4053FG NC010 Polyester Elastomer TPC-ET  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
40 Shore D High Performance Polyester Elastomer Developed for Food Contact ApplicationsInformation provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.02 g/cc
0.0368 lb/in³
1.16 g/cc
0.0419 lb/in³
ISO 1183
Water Absorption 0.70 %

@Thickness 2.00 mm
0.70 %

@Thickness 0.0787 in
Sim. to ISO 62
Moisture Absorption 0.200 %

@Thickness 2.00 mm
0.200 %

@Thickness 0.0787 in
Sim. to ISO 62
Linear Mold Shrinkage, Flow 0.0020 cm/cm
0.0020 in/in
ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.0040 cm/cm
0.0040 in/in
ISO 294-4 2577
Melt Flow 5.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
5.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
cm³/10min; ISO 1133
5.3 g/10 min

@Load 2.16 kg,
Temperature 190 °C
5.3 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ISO 1133
Mechanical Properties Metric English Comments
Hardness, Shore D 38
38
15s; ISO 868
Tensile Strength at Break 26.0 MPa
3770 psi
ISO 527-1/-2
Tensile Stress 2.40 MPa

@Strain 5.00 %
348 psi

@Strain 5.00 %
ISO 527-1/-2
4.10 MPa

@Strain 10.0 %
595 psi

@Strain 10.0 %
ISO 527-1/-2
7.30 MPa

@Strain 50.0 %
1060 psi

@Strain 50.0 %
ISO 527-1/-2
Elongation at Break >= 300 %
>= 300 %
ISO 527-1/-2
Tensile Modulus 0.0560 GPa
8.12 ksi
ISO 527-1/-2
Charpy Impact Unnotched NB
NB
ISO 179/1eU
NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
ISO 179/1eU
Charpy Impact, Notched NB
NB
ISO 179/1eA
NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
ISO 179/1eA
NB

@Temperature -40.0 °C
NB

@Temperature -40.0 °F
ISO 179/1eA
Tensile Impact Strength 230 kJ/m²
109 ft-lb/in²
notched; ISO 8256/1
Tensile Creep Modulus, 1 hour 50.0 MPa

@Time 3600 sec
7250 psi

@Time 1.00 hour
ISO 899-1
Tensile Creep Modulus, 1000 hours 40.0 MPa

@Time 3.60e+6 sec
5800 psi

@Time 1000 hour
ISO 899-1
Tear Strength 110 kN/m
628 pli
parallel; ISO 34-1
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 220 µm/m-°C
122 µin/in-°F
ISO 11359-1/-2
CTE, linear, Transverse to Flow 220 µm/m-°C
122 µin/in-°F
ISO 11359-1/-2
Melting Point 150 °C
302 °F
10°C/min; ISO 11357-1/-3
Glass Transition Temp, Tg -50.0 °C
-58.0 °F
10°C/min; ISO 11357-1/-2
Flammability, UL94 HB

@Thickness 1.50 mm
HB

@Thickness 0.0591 in
IEC 60695-11-10
Oxygen Index 20 %
20 %
ISO 4589-1/-2
Electrical Properties Metric English Comments
Volume Resistivity 7.00e+12 ohm-cm
7.00e+12 ohm-cm
IEC 60093
Surface Resistance 2.00e+14 ohm
2.00e+14 ohm
IEC 60093
Dielectric Constant 4.7

@Frequency 1.00e+6 Hz
4.7

@Frequency 1.00e+6 Hz
IEC 60250
5.2

@Frequency 100 Hz
5.2

@Frequency 100 Hz
IEC 60250
Dielectric Strength 18.0 kV/mm
457 kV/in
IEC 60243-1
Dissipation Factor 0.011

@Frequency 100 Hz
0.011

@Frequency 100 Hz
IEC 60250
0.0525

@Frequency 1.00e+6 Hz
0.0525

@Frequency 1.00e+6 Hz
IEC 60250
Comparative Tracking Index 600 V
600 V
IEC 60112
Descriptive Properties Value Comments
Delivery Form Pellets
Eff. thermal diffusivity 5.44E-08 m²/s
Part Marking Code >TPC-ET<
ISO 11469
Processing Calandering
Casting
Coatable
Film Extrusion
Injection Moulding
Other Extrusion
Profile Extrusion
Sheet Extrusion
Thermoforming
Regional Availability Asia Pacific
Europe
Global
Near East/Africa
North America
South and Central America
Resin Identification TPC-ET
ISO 1043
Special Characteristics Light stabilised or stable to light
UL recognition UL