Denka TH-21 Transparent Resin Polymer (MBS resin) Polymethacrylate Butadiene Styrene

Category Polymer , Thermoplastic , Styrene-Butadiene
Manufacturer Denka
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Denka TH-21 Transparent Resin Polymer (MBS resin) Polymethacrylate Butadiene Styrene.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
"TX Polymer" (methyl methacrylate styrene), MS resins as an alternative to acrylic resins, with low density, low moisture absorption, and good moldability, "TH Polymer/TP Polymer," MBS resins with a good balance of transparency, strength and fluidity (methyl methacrylate butadiene styrene), "TE Series/CL Series," transparent ABS resins with excellent color attributes and tensile strength are available (among others).ApplicationsTX is used for:flat display substratesoptical componentsmiscellaneous goods.TP/TH are used for:food package sheeting as well as in manufacturingelectronic equipment and componentsmiscellaneous goodsTE/CL are for:electronic equipment and componentsinformation equipment componentsAV equipment, etc.
Physical Properties Metric English Comments
Specific Gravity 1.10 g/cc
1.10 g/cc
ASTM D792
Density 1.085 g/cc
0.03920 lb/in³
ISO 1183
Melt Flow 3.9 g/10 min

@Load 5.00 kg,
Temperature 200 °C
3.9 g/10 min

@Load 11.0 lb,
Temperature 392 °F
ISO 1133
47 g/10 min

@Load 10.0 kg,
Temperature 220 °C
47 g/10 min

@Load 22.0 lb,
Temperature 428 °F
ISO 1133
Mechanical Properties Metric English Comments
Hardness, Rockwell M 39
39
ISO 2039-2
Tensile Strength at Break 36.0 MPa
5220 psi
50mm/min; ISO 527-2
45.0 MPa
6530 psi
50mm/min; ASTM D638
Elongation at Break 30 %
30 %
50mm/min; ISO 527-2
Flexural Strength 72.0 MPa
10400 psi
ISO 178
73.0 MPa
10600 psi
2mm/min; ASTM D790
Flexural Modulus 2.40 GPa
348 ksi
2mm/min; ISO 178
2.42 GPa
351 ksi
2mm/min; ASTM D790
Izod Impact Resistance 8.50 J/cm²
40.5 ft-lb/in²
Charpy Impact, Notched 1.10 J/cm²
5.24 ft-lb/in²
ISO 179-2
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 65.0 °C
149 °F
ISO 75-2
73.0 °C
163 °F
ASTM D648
Vicat Softening Point 86.0 °C
187 °F
50N; ISO 306
Flammability, UL94 HB
HB
Optical Properties Metric English Comments
Haze 2.4 %

@Thickness 2.00 mm
2.4 %

@Thickness 0.0787 in
ISO 14782
Transmission, Visible 91 %

@Thickness 2.00 mm
91 %

@Thickness 0.0787 in
ISO 13468-1