DSM Arnite® TM4 440 (PBT+PET)-MD20
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , PBT + PET, Mineral Filled |
| Manufacturer | DSM Engineering Plastics |
| Trade Name | Arnite® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DSM Arnite® TM4 440 (PBT+PET)-MD20.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
20% Mineral Reinforced
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.48 g/cc | 0.0535 lb/in³ | ISO 1183 |
| Water Absorption | 0.35 % | 0.35 % | Sim. To ISO 62 |
| Moisture Absorption | 0.150 % | 0.150 % | Sim. To ISO 62 |
| Viscosity | 17500 cP @Shear Rate 100000 1/s, Temperature 280 °C |
17500 cP @Shear Rate 100000 1/s, Temperature 536 °F |
|
| 20000 cP @Shear Rate 100000 1/s, Temperature 250 °C |
20000 cP @Shear Rate 100000 1/s, Temperature 482 °F |
||
| 25000 cP @Shear Rate 100000 1/s, Temperature 230 °C |
25000 cP @Shear Rate 100000 1/s, Temperature 446 °F |
||
| 200000 cP @Shear Rate 1.00 1/s, Temperature 280 °C |
200000 cP @Shear Rate 1.00 1/s, Temperature 536 °F |
||
| 500000 cP @Shear Rate 1.00 1/s, Temperature 250 °C |
500000 cP @Shear Rate 1.00 1/s, Temperature 482 °F |
||
| 1.15e+6 cP @Shear Rate 1.00 1/s, Temperature 230 °C |
1.15e+6 cP @Shear Rate 1.00 1/s, Temperature 446 °F |
||
| Linear Mold Shrinkage, Flow | 0.014 cm/cm | 0.014 in/in | Sim. To ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.017 cm/cm | 0.017 in/in | Sim. To ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 57.0 MPa | 8270 psi | ISO 527-1/-2 |
| Elongation at Break | 2.4 % | 2.4 % | ISO 527-1/-2 |
| Tensile Modulus | 4.70 GPa | 682 ksi | ISO 527-1/-2 |
| Charpy Impact Unnotched | 3.50 J/cm² @Temperature 23.0 °C |
16.7 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU |
| Charpy Impact, Notched | 0.200 J/cm² @Temperature 23.0 °C |
0.952 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 195 °C | 383 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C | 212 °F | ISO 75-1/-2 |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
IEC 60695-11-10 |
Users viewing this material also viewed the following:
- Quadrant EPP Proteus® LSG HS PP - Heat Stabilized Polypropylene (ASTM Product Data Sheet)
- Overview of materials for Polystyrene, Wood Filled
- Michelman® Michem® In-Line Primer Q4325A Primer
- SABIC Innovative Plastics LNP THERMOTUF VF006U Super Tough Nylon
- A. Schulman POLYAXIS® PD2000 Polypropylene
- A. Schulman POLYBATCH™ White P8555 T2 Concentrate Based In Homopolymer Polypropylene
- ExxonMobil Bicor™ 15MB440 OPP Film
- ExxonMobil QQ Mobiltac Double Letter Series
Copyright © lookpolymers.com All Rights Reserved