- Covestro Apec® HT KU 1-9357/2 High-Heat Polycarbonate, 20% Glass Fiber
Covestro Apec® HT KU 1-9357/2 High-Heat Polycarbonate, 20% Glass Fiber
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Glass Fiber Filled, Flame Retardant |
| Manufacturer | Covestro |
| Trade Name | Apec® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Covestro Apec® HT KU 1-9357/2 High-Heat Polycarbonate, 20% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Only opaque colors available, with 20% glass fiber reinforcement, flame retardant.Applications: Lighting, electrical parts.Information provided by Bayer.As of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and officially adopted its new name – Covestro.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.30 g/cc | 0.0470 lb/in³ | |
| Water Absorption | 0.35 % | 0.35 % | Saturation in water |
| Moisture Absorption at Equilibrium | 0.15 % | 0.15 % | Equilibrium at 50% RH |
| Water Absorption at Saturation | 0.35 % | 0.35 % | |
| Melt Flow | 6.0 g/10 min @Load 2.16 kg, Temperature 330 °C |
6.0 g/10 min @Load 4.76 lb, Temperature 626 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 100 MPa | 14500 psi | |
| Elongation at Break | 3.0 % | 3.0 % | |
| Tensile Modulus | 5.90 GPa | 856 ksi | |
| Charpy Impact Unnotched | 5.00 J/cm² | 23.8 ft-lb/in² | |
| 0.800 J/cm² @Temperature -30.0 °C |
3.81 ft-lb/in² @Temperature -22.0 °F |
||
| Charpy Impact, Notched | 0.800 J/cm² | 3.81 ft-lb/in² |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 30.0 µm/m-°C @Temperature 20.0 °C |
16.7 µin/in-°F @Temperature 68.0 °F |
|
| CTE, linear, Transverse to Flow | 60.0 µm/m-°C @Temperature 20.0 °C |
33.3 µin/in-°F @Temperature 68.0 °F |
|
| Deflection Temperature at 0.46 MPa (66 psi) | 184 °C | 363 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 178 °C | 352 °F | |
| Vicat Softening Point | 186 °C | 367 °F | |
| Flammability, UL94 | V-0 @Thickness 1.60 mm |
V-0 @Thickness 0.0630 in |
|
| V-0 @Thickness 3.00 mm |
V-0 @Thickness 0.118 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | |
| Dielectric Constant | 3.1 @Frequency 1e+6 Hz |
3.1 @Frequency 1e+6 Hz |
|
| 3.2 @Frequency 100 Hz |
3.2 @Frequency 100 Hz |
||
| Dielectric Strength | 38.0 kV/mm | 965 kV/in | |
| Dissipation Factor | 0.0015 @Frequency 100 Hz |
0.0015 @Frequency 100 Hz |
|
| 0.0088 @Frequency 1e+6 Hz |
0.0088 @Frequency 1e+6 Hz |
||
| Comparative Tracking Index | 200 V | 200 V |