Clariant Renol PA211G13 Nylon 6, 13% Glass Fiber
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 10% Glass Fiber Filled |
| Manufacturer | Clariant |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Clariant Renol PA211G13 Nylon 6, 13% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by Clariant Masterbatches
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.22 g/cc | 1.22 g/cc | ASTM D792 |
| Filler Content | 13 % | 13 % | ASTM D2584 |
| Linear Mold Shrinkage, Flow | 0.0050 cm/cm | 0.0050 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 96.5 MPa | 14000 psi | ASTM D638 |
| Elongation at Yield | 3.0 % | 3.0 % | ASTM D638 |
| Flexural Yield Strength | 128 MPa | 18500 psi | ASTM D790 |
| Flexural Modulus | 4.83 GPa | 700 ksi | ASTM D790 |
| Izod Impact, Notched | 0.481 J/cm @Temperature 22.8 °C |
0.900 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 199 °C | 390 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 238 - 260 °C | 460 - 500 °F | |
| Mold Temperature | 79.4 - 107 °C | 175 - 225 °F | |
| Dry Time | 2 - 4 hour @Temperature 79.4 °C |
2 - 4 hour @Temperature 175 °F |
to ensure moisture content is less than 0.2% |
| Injection Pressure | 4.96 - 8.27 MPa | 720 - 1200 psi | Secondary |
| 8.27 - 13.8 MPa | 1200 - 2000 psi | Initial | |
| Back Pressure | 0.000 - 0.345 MPa | 0.000 - 50.0 psi | |
| Shot Size | 30 - 80 % | 30 - 80 % | |
| Screw Speed | 20 - 100 rpm | 20 - 100 rpm |
Users viewing this material also viewed the following:
- MV Labs NH200 NH4Br Ammonium bromide
- Schwartz Technical Plastics LAMIGAMID® 317 Cast Polyamide 6, Heat Stabilized, Dry
- Teknor Apex Telcar® TL-2596C Thermoplastic Elastomer
- Cosmic Plastics K61 Long Glass Fiber Filled Iso Diallyl Phthalate Molding Compound
- The Chemical Company FCC Food Grade DL-Malic Acid, C4H4O4
- A. Schulman POLYBATCH™ Beige 1266E Concentrate Based In Polyethylene
- Fainplast Compounds GA 0179 Flexible PVC, Flame Retardant Sheathing
- AK Steel 420HC Martensitic Stainless steel
- Henkel Hysol MA 562SFR Core Splice Adhesive
Copyright © lookpolymers.com All Rights Reserved