- CeramTec CD 101 Silicon Carbide, SiC-ZrB2
CeramTec CD 101 Silicon Carbide, SiC-ZrB2
| Category | Ceramic , Carbide |
| Manufacturer | CeramTec North America |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | CeramTec CD 101 Silicon Carbide, SiC-ZrB2.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
CD101 is a zirconia reinforced silicon carbide designed for maximum hardness.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 3.26 g/cc | 0.118 lb/in³ | DIN EN 623-2 |
| Water Absorption | 0.00 % | 0.00 % | DIN EN 623-2 |
| Porosity | 2.0 % | 2.0 % | closed (approximate vol. %) |
| Permeability | 0.00 | 0.00 | %, Gas |
| Weibull Modulus | 8.0 | 8.0 | DINV ENV 843-5 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Vickers Microhardness | 2750 | 2750 | HV 0.5; DINV ENV 843-4 |
| Tensile Strength at Break | 330 MPa | 47900 psi | ACMA Test #4 / DIN EN 843-1 |
| Tensile Modulus | 415 GPa | 60200 ksi | Young's; DINV ENV 843-2 |
| Flexural Strength | 330 MPa | 47900 psi | DIN EN 843-1 |
| 360 MPa | 52200 psi | Bending Strength; 4-Point Method (40x4x3 mm³); ASTM-F417 | |
| Compressive Strength | 2000 MPa | 290000 psi | DIN 51067T1 |
| Poissons Ratio | 0.16 | 0.16 | DINV ENV 843-2 |
| Fracture Toughness | 3.80 MPa-m½ | 3.46 ksi-in½ | K<sub>IC</sub>; DIN 51109 |
| Shear Modulus | 179 GPa | 26000 ksi | Calculated |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 3.50 µm/m-°C @Temperature 20.0 - 200 °C |
1.94 µin/in-°F @Temperature 68.0 - 392 °F |
DIN EN 821-1 |
| 3.50 µm/m-°C @Temperature 20.0 - 400 °C |
1.94 µin/in-°F @Temperature 68.0 - 752 °F |
DIN EN 821-1 | |
| 4.50 µm/m-°C @Temperature 20.0 - 600 °C |
2.50 µin/in-°F @Temperature 68.0 - 1110 °F |
DIN EN 821-1 | |
| 4.50 µm/m-°C @Temperature 20.0 - 1000 °C |
2.50 µin/in-°F @Temperature 68.0 - 1830 °F |
DIN EN 821-1 | |
| Specific Heat Capacity | 0.600 J/g-°C @Temperature 20.0 - 100 °C |
0.143 BTU/lb-°F @Temperature 68.0 - 212 °F |
DINV ENV 821-3 |
| Thermal Conductivity | 100 W/m-K @Temperature 20.0 - 100 °C |
694 BTU-in/hr-ft²-°F @Temperature 68.0 - 212 °F |
DIN EN 821-2 |
| Maximum Service Temperature, Air | 1400 °C | 2550 °F | |
| Maximum Service Temperature, Inert | 1800 °C | 3270 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 0.10 ohm-cm @Temperature 500 °C |
>= 0.10 ohm-cm @Temperature 932 °F |
|
| >= 100 ohm-cm @Temperature 400 °C |
>= 100 ohm-cm @Temperature 752 °F |
IEC 672-1 | |
| >= 30000 ohm-cm @Temperature 20.0 °C |
>= 30000 ohm-cm @Temperature 68.0 °F |
IEC 672-1 | |
| Dielectric Constant | 29 @Frequency 1.00e+6 Hz |
29 @Frequency 1.00e+6 Hz |
IEC 672-1 |
| Dielectric Loss Index | 0.20 @Frequency 9.00e+9 Hz |
0.20 @Frequency 9.00e+9 Hz |
IEC 672-1 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Black | |
| Thermal Shock Resistance R1 (K) | 191 | R1 = [s? (1-µ)] / (a·E) |
Users viewing this material also viewed the following:
- Polimeri Europa Dutral® TER 6537 Ethylene - Propylene - Diene Terpolymer
- Nilit FRIANYL A63 W-GV25 Nylon 6.6, std. viscosity for injection molding, 25% glass fiber reinforced
- PolyOne Geon™ Vinyl Dry Blend E7000 Polyvinyl Chloride, Rigid (PVC, Rigid)
- Sumitomo Bakelite Durez® 152 Phenolic, Compression Grade
- SABIC Innovative Plastics Noryl GTX LMX171 PPO/PBT (Europe-Africa-Middle East)
- Zhejiang Juner PA-A7-1 Flame-Retardant & Glass Reinforced, Environmental PA66
- CPC - Vycom SEABOARD™ LITE High density polyethylene (HDPE)
- ExxonMobil 68 Mobil EAL Arctic Series
Copyright © lookpolymers.com All Rights Reserved