Bulk Molding Compounds BMC 501E Mineral Filled, Glass Reinforced Polyester

Category	Polymer , Thermoset , Filled/Reinforced Thermoset , Polyester, TS , Thermoset Polyester Glass and Mineral Filled BMC
Manufacturer	BMC - Bulk Molding Compounds Inc.
Trade Name	BMC
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Bulk Molding Compounds BMC 501E Mineral Filled, Glass Reinforced Polyester.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

BMC 501E molding compound is a mineral filled, glass-fiber-reinforced polyester compound suitable for compression and transfer molding. It is a product with good overall electrical properties, flame resistance, and low water absorption. Distinguished from other materials by its very soft flow, it is an excellent compound for encapsulating delicate components.Typical applications include coil and solenoid Encapsulation.

Physical Properties	Metric	English	Comments
Specific Gravity	1.77 g/cc	1.77 g/cc
Water Absorption	0.10 %	0.10 %	24 hours, 23°C
Linear Mold Shrinkage	0.00 - 0.0015 cm/cm	0.00 - 0.0015 in/in

Mechanical Properties	Metric	English
Hardness, Barcol	<= 10	<= 10
Tensile Strength, Ultimate	27.6 - 41.4 MPa	4000 - 6000 psi
Flexural Strength	68.9 - 82.7 MPa	10000 - 12000 psi
Compressive Strength	75.8 - 103 MPa	11000 - 15000 psi
Izod Impact, Notched	0.801 - 1.60 J/cm	1.50 - 3.00 ft-lb/in

Thermal Properties	Metric	English
Deflection Temperature at 1.8 MPa (264 psi)	>= 204 °C	>= 400 °F
Flammability, UL94	V-0 @Thickness 6.35 mm	V-0 @Thickness 0.250 in
	V-0 @Thickness 3.17 mm	V-0 @Thickness 0.125 in
	V-0 @Thickness 1.59 mm	V-0 @Thickness 0.0625 in

Electrical Properties	Metric	English	Comments
Dielectric Constant	4.9 @Frequency 60 Hz	4.9 @Frequency 60 Hz
Dielectric Strength	11.8 kV/mm	300 kV/in	Short Time
Dissipation Factor	0.0070 @Frequency 60 Hz	0.0070 @Frequency 60 Hz
Arc Resistance	>= 180 sec	>= 180 sec
Comparative Tracking Index	>= 500 V	>= 500 V

Processing Properties	Metric	English	Comments
Mold Temperature	138 - 166 °C	280 - 330 °F