Bulk Molding Compounds BMC 1608 Very High Strength, Corrosion Resistant

Category	Polymer , Thermoset , Polyester, TS
Manufacturer	BMC - Bulk Molding Compounds Inc.
Trade Name	BMC
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Bulk Molding Compounds BMC 1608 Very High Strength, Corrosion Resistant.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

BMC 1608 is a very high strength, general purpose, corrosion resistant material. Recommended for compression molding only. UL® recognized. Meets FDA requirements for food contact. This material was formerly known as Glastic® 1608.

Physical Properties	Metric	English	Comments
Specific Gravity	1.75 - 1.80 g/cc	1.75 - 1.80 g/cc
Water Absorption	0.12 - 0.20 %	0.12 - 0.20 %	24 hours, 23°C
Linear Mold Shrinkage	0.0010 - 0.0030 cm/cm	0.0010 - 0.0030 in/in

Mechanical Properties	Metric	English
Hardness, Barcol	40 - 50	40 - 50
Tensile Strength, Ultimate	34.5 - 41.4 MPa	5000 - 6000 psi
Flexural Strength	193 - 200 MPa	28000 - 29000 psi
Flexural Modulus	13.8 - 15.2 GPa	2000 - 2200 ksi
Compressive Strength	234 - 241 MPa	34000 - 35000 psi
Izod Impact, Notched	4.81 - 5.34 J/cm	9.00 - 10.0 ft-lb/in

Thermal Properties	Metric	English	Comments
Deflection Temperature at 1.8 MPa (264 psi)	>= 260 °C	>= 500 °F
Flammability, UL94	HB	HB

Electrical Properties	Metric	English	Comments
Dielectric Strength	17.6 kV/mm	447 kV/in	Short Time
Dissipation Factor	0.0050 @Frequency 60 Hz	0.0050 @Frequency 60 Hz	Condition A
	0.0080 @Frequency 60 Hz	0.0080 @Frequency 60 Hz	Condition A
	0.026 @Frequency 60 Hz	0.026 @Frequency 60 Hz	Condition D
	0.115 @Frequency 60 Hz	0.115 @Frequency 60 Hz	Condition D
Arc Resistance	104 sec	104 sec
Track Resistance	1.75 sec	1.75 sec

Processing Properties	Metric	English	Comments
Mold Temperature	138 - 166 °C	280 - 330 °F