Polymer Property : Compressive Strength = 34000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Compressive Strength	234 MPa @Thickness 12.7 mm	34000 psi @Thickness 0.500 in	ASTM D695
Industrial Laminates/Norplex NP310 Cotton Fabric Description: Canvas machining grade for structural and mechanical applications. Better impact strength than phenolic paper grades. MIL-I-24768/16. Thickness Tested: 0.062, 0.125", and 0.500".
Compressive Strength	234 MPa @Thickness 12.7 mm	34000 psi @Thickness 0.500 in	ASTM D695
Industrial Laminates/Norplex NP310E Cotton Fabric Description: Manufactured with a domestic cotton fabric and phenolic resin. Similar to NP310 with improved moisture resistance and electrical properties. Mechanical properties equivalent to NP310. M..
Compressive Strength	234 MPa @Thickness 12.7 mm	34000 psi @Thickness 0.500 in	ASTM D695
Industrial Laminates/Norplex NP329 Cotton Fabric Description: Bleached linen with melamine resin system. Provides better arc resistance than NP320E. Also, resistant to ammonia based refrigerants. Hard, durable material should be heated to punch, ..
Compressive Strength	234 - 241 MPa	34000 - 35000 psi
Bulk Molding Compounds BMC 1608 Very High Strength, Corrosion Resistant BMC 1608 is a very high strength, general purpose, corrosion resistant material. Recommended for compression molding only. UL® recognized. Meets FDA requirements for food contact. This material was..
Compressive Strength	234 MPa @Thickness 12.7 mm	34000 psi @Thickness 0.500 in	ASTM D695
Industrial Laminates/Norplex NP321 Cotton Fabric (discontinued **) Description: NP321 consists of a fine weave cotton fabric (linen) impregnated with a phenolic resin binder. Applications include vanes for air and liquid pumps, and compressors. NP321 remains very f..