BASF Ultramid® 82335G HS BK 102 50% Glass Filled PA6 (Conditioned)

Category	Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 50% Glass Fiber Filled
Manufacturer	BASF
Trade Name	Ultramid®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	BASF Ultramid® 82335G HS BK 102 50% Glass Filled PA6 (Conditioned).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Description: Ultramid 8235G HS BK-102 is a heat stabilized, pigmented black, 50% glass fiber reinforced PA6 injection molding compound offering excellent level of strength, stiffness, high temperature performance and dimensional stability. Its resistance to creep under load is excellent. It is available in natural, black, weather resistance and pigmented versions.Applications: Ultramid 8235G HS BK-102 is generally recommended for applications such as power tool housings, cattle ear taggers, luggage frames, fans and pressure regulator housings.Information provided by BASF

Physical Properties	Metric	English	Comments
Density	1.56 g/cc	0.0564 lb/in³	ISO 1183
Moisture Absorption at Equilibrium	1.4 %	1.4 %	50% RH; ISO 62
	4.8 %	4.8 %	Saturation; ISO 62

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	145 MPa	21000 psi	ISO 527
Elongation at Break	6.0 %	6.0 %	ISO 527
Tensile Modulus	8.91 GPa	1290 ksi	ISO 527

Processing Properties	Metric	English
Melt Temperature	280 - 305 °C	536 - 581 °F
Mold Temperature	80.0 - 95.0 °C	176 - 203 °F
Drying Temperature	80.0 °C	176 °F
Dry Time	2 - 4 hour	2 - 4 hour
Moisture Content	>= 0.060 %	>= 0.060 %
Injection Pressure	35.0 - 125 MPa	5080 - 18100 psi

Descriptive Properties	Value	Comments
Color	BK 102
Commercial Status	North America