ExxonMobil Label-Lyte™ 65LT500 OPP Film
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Film Grade |
| Manufacturer | Exxon Chemical |
| Trade Name | Label-Lyte™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | ExxonMobil Label-Lyte™ 65LT500 OPP Film.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Product Description: A matte finish, white polypropylene film designed or use in demanding thermal transfer, pressure-sensitive label and tag applications.Availability: Asia Pacific, Europe and North AmericaKey Features: Excellent print resolution and abrasionWide compatibility with Thermal Transfer RibbonsExcellent barcode scan capabilityExcellent static resistant propertiesFeatures:Adhesive Receptive CoatedStatic Resistant Matte CoatedApplications:AutomotiveHealth and Beauty CareHousehold and DetergentsIndustrialPharmaceuticalsRetail, shelf marking, barcodesUses: Pressure Sensitive LabelsUnsupported Labels & TagsProcessing Method: Surface Print Unsupported, Thermal Transfer Printing, UV Flexographic Printing, UV Letterpress Printing, UV Screen Printing and Water-based Flexographic PrintingInformation provided by ExxonMobil
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Thickness | 66.0 microns | 2.60 mil | ExxonMobil Method |
| Coating Weight | 48.0 g/m² | 30.0 lb/ream | ExxonMobil Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Elongation at Break, MD | 170 % | 170 % | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Film Elongation at Break, TD | 55 % | 55 % | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Film Tensile Strength at Break, MD | 105 MPa | 15200 psi | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Film Tensile Strength at Break, TD | 185 MPa | 26800 psi | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Shrinkage, MD | 4.0 % @Temperature 135 °C, Time 432 sec |
4.0 % @Temperature 275 °F, Time 0.120 hour |
ExxonMobil Method |
| Shrinkage, TD | 2.0 % @Temperature 135 °C, Time 432 sec |
2.0 % @Temperature 275 °F, Time 0.120 hour |
ExxonMobil Method |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Gloss | 10 % | 10 % | 45°; ExxonMobil Method |
| Transmission, Visible | 20 % | 20 % | ExxonMobil Method |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Stiffness (Gurley) | 17 mgf | MD |
| 30 mgf | TD | |
| Yield | 14400 in2/lb |
Users viewing this material also viewed the following:
- Northstar Polymers SBX-146 Curing Agent
- SABIC Innovative Plastics Lexan® IR1810 PC (Europe-Africa-Middle East)
- Global GG-3245 High Density Polyethylene, Blow Molding Grade
- Lubriplate SYNX HD-2 Calcium Sulfonate Complex Multi-Purpose Grease
- Hexcel® HexWeb® HRP - 3/16 - 4.0 Fiberglass/Phenolic Honeycomb
- Lubrizol ESTANE® 5701 Ester Based Thermoplastic Polyurethane
- ELASTO UK Dryflex® 660750S SEBS Based Material, Semi-Filled Qualities, 75A Hardness, Natural
- DuPont Performance Polymers Sorona® 3030GV NC010 Polytrimethylene Terephthalate (PTT)
- Aclo Accutech Nylon 6 NY0730G30L Glass Reinforced
- BASF Ecoflex® P BX 7020 Biodegradable Polyester
Copyright © lookpolymers.com All Rights Reserved