Category Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Impact Modified
Manufacturer Azoty Tarnow™ (Zaklady Azotowe)
Trade Name TARNOFORM
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Azoty Tarnow™ TARNOFORM 300 CI2 POM.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Impact modified injection molding grade based on Tarnoform 300 reinforced with 10% MBS rubber yielding good cold impact strength and good strength of weld lines combined with good weatherability.Information provided by Zakłady Azotowe w Tarnowie-Moscicach S.A.
Physical Properties Metric English Comments
Density 1.34 g/cc
0.0484 lb/in³
ISO 1183
Water Absorption 0.26 %
0.26 %
ISO 62
Melt Flow 5.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
5.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ISO 1133
Mechanical Properties Metric English Comments
Hardness, Rockwell R 110
110
ISO 2039-2
Ball Indentation Hardness 120 MPa
17400 psi
358 N; ISO 2039-1
Tensile Strength, Yield 49.0 MPa
7110 psi
ISO 527
Elongation at Break 55 %
55 %
ISO 527
Flexural Strength 52.0 MPa
7540 psi
ISO 178
Izod Impact, Notched (ISO) 11.0 kJ/m²
5.24 ft-lb/in²
1A; ISO 180
Charpy Impact, Notched 1.20 J/cm²
5.71 ft-lb/in²
1eA; ISO 179
Thermal Properties Metric English Comments
Melting Point 170 °C
338 °F
10°C/min.; ISO 3146
Deflection Temperature at 1.8 MPa (264 psi) 81.0 °C
178 °F
ISO 75
Vicat Softening Point 143 °C
289 °F
50 N; ISO 306
Flammability, UL94 HB

@Thickness 3.20 mm
HB

@Thickness 0.126 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+14 ohm-cm
1.00e+14 ohm-cm
IEC 60093
Surface Resistance 1.00e+13 ohm
1.00e+13 ohm
IEC 60093
Dielectric Constant 4.3

@Frequency 1e+6 Hz
4.3

@Frequency 1e+6 Hz
IEC 60250
Dielectric Strength 40.0 kV/mm
1020 kV/in
IEC 60243
Dissipation Factor 0.00060

@Frequency 1e+6 Hz
0.00060

@Frequency 1e+6 Hz
IEC 60250
Comparative Tracking Index 600 V
600 V
IEC 112
Processing Properties Metric English Comments
Processing Temperature 180 - 210 °C
356 - 410 °F
Barrel temperature
Mold Temperature 60.0 - 80.0 °C
140 - 176 °F