Asahi Kasei Xyron® A0210 PPE/PA

Category	Polymer , Thermoplastic , Nylon , Polyphenylene Ether/PPO , Polyphenylene Ether, Molded
Manufacturer	Asahi Kasei
Trade Name	Xyron®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Asahi Kasei Xyron® A0210 PPE/PA.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

AutomotiveInformation provided by Asahi Kasei

Physical Properties	Metric	English	Comments
Specific Gravity	1.09 g/cc	1.09 g/cc	23°C; ASTM D792
Moisture Absorption	0.600 %	0.600 %	23°C, 50% RH 24 hours; ASTM D570
Linear Mold Shrinkage	0.011 - 0.014 cm/cm	0.011 - 0.014 in/in	ASTM D955

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	68.0 MPa	9860 psi	23°C, 50% RH; ASTM D638
Elongation at Break	48 %	48 %	23°C, 50% RH; ASTM D638
Flexural Strength	107 MPa	15500 psi	23°C, 50% RH; ASTM D790
Flexural Modulus	2.62 GPa	380 ksi	23°C, 50% RH; ASTM D790
Izod Impact, Notched	2.50 J/cm @Thickness 6.40 mm, Temperature 23.0 °C	4.68 ft-lb/in @Thickness 0.252 in, Temperature 73.4 °F	ASTM D256

Thermal Properties	Metric	English	Comments
CTE, linear	90.0 µm/m-°C @Temperature -30.0 - 60.0 °C	50.0 µin/in-°F @Temperature -22.0 - 140 °F	ASTM D696
Deflection Temperature at 0.46 MPa (66 psi)	190 °C	374 °F	ASTM D648
Flammability, UL94	HB @Thickness 1.60 mm	HB @Thickness 0.0630 in	Equivalant
	HB @Thickness 3.20 mm	HB @Thickness 0.126 in	Equivalant

Processing Properties	Metric	English	Comments
Processing Temperature	280 - 300 °C	536 - 572 °F	Resin Temperature
Mold Temperature	60.0 - 100 °C	140 - 212 °F
Drying Temperature	100 - 110 °C	212 - 230 °F	Pre-drying Temperature
Dry Time	3 - 4 hour	3 - 4 hour