Songhan Plastic Technology Co.,Ltd.
 POLYMER SEARCH

Arlon 61089R040 0.040" (1.02 mm) Uncured/Cured Silicone Rubber with Denier Vectran HS Substrate

Category Polymer , Thermoset , Silicone , Silicone Rubber , Silicone, Molded, Glass Fiber Filled
Manufacturer Arlon
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Arlon 61089R040 0.040" (1.02 mm) Uncured/Cured Silicone Rubber with Denier Vectran HS Substrate.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Design/Construction: Interleave: Polyethylene Layer 2: Uncured Silicone Rubber Layer 1: Cured Silicone Rubber Substrate: 1000 Denier Vectran HS Appearance: Red silicone gum on Vectran fabricThis data represents typical values for the production material. The data should not be used to write, or in place of, material specifications.Information provided by Arlon, Silicone Technologies Division
Physical Properties Metric English Comments
Density 1.375 g/cc
0.04968 lb/in³
Silicone Property; Arlon SQA-TMS-024
Thickness 63.5 microns
2.50 mil
Interleave
152 microns
6.00 mil
Layer 2; Arlon SQA-TMS-003
356 microns
14.0 mil
Layer 1; Arlon SQA-TMS-003
508 microns
20.0 mil
Substrate; Arlon SQA-TMS-003
1020 microns
40.0 mil
Overall; Arlon SQA-TMS-003
Mechanical Properties Metric English Comments
Hardness, Shore A 35
35
Silicone Property; ASTM D2240
Tensile Strength 6.21 MPa
900 psi
Silicone Property; ASTM D412
Elongation at Break 750 %
750 %
Silicone Property; ASTM D412
Peel Strength 7.05 kN/m
40.2 pli
(S1 to S1) Bond Strength; Arlon SQA -TMS-011
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 232 °C
450 °F
Minimum Service Temperature, Air -56.7 °C
-70.0 °F
Flammability Test <= 3.0
<= 3.0
[in], Char Length; FAR25.853 Appendix F Pt. 1 Section (a),(1).(ii)
<= 15
<= 15
[sec], Flame and Glow Time; FAR25.853 Appendix F Pt. 1 Section (a),(1).(ii)
Electrical Properties Metric English Comments
Dielectric Strength 18.2 kV/mm
462 kV/in
ASTM D149
Processing Properties Metric English Comments
Cure Time 120 min

@Temperature 204 °C
2.00 hour

@Temperature 400 °F
Recommended Postcure Cycle
15.0 min

@Pressure 0.345 MPa,
Temperature 121 °C
0.250 hour

@Pressure 50.0 psi,
Temperature 250 °F
Recommended Cure Cycle
Shelf Life 6.00 Month

@Temperature 21.1 °C
6.00 Month

@Temperature 70.0 °F
From date of manufacture
Descriptive Properties Value Comments
Color Light Yellow
Substrate
Red
Total Product Weight (oz/yd2) 35.3
Arlon SQA-TMS-025