Arkema Group Orgalloy® LT 6040 Flexible Nylon Alloy (Conditioned)
| Category | Polymer , Thermoplastic , Nylon , Nylon, Flexible Alloy |
| Manufacturer | Arkema |
| Trade Name | Orgalloy® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Arkema Group Orgalloy® LT 6040 Flexible Nylon Alloy (Conditioned).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Very flexible polyamide alloy: easy to process, low moisture absorption, good mechanical properties at low temperature. Demonstrate a good balance of properties eg, high flexibility (500 MPa), good thermal performance and ductility at low temperatures.Suited to the extrusion of mandrels and for blow molding of technical parts under the hood (air intake).ISO data provided by the manufacturer, Arkema.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.08 g/cc | 0.0390 lb/in³ | |
| Melt Flow | 5.5 g/10 min @Load 5.00 kg, Temperature 235 °C |
5.5 g/10 min @Load 11.0 lb, Temperature 455 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 27.0 MPa | 3920 psi | 50 mm/min |
| Elongation at Break | >= 50 % | >= 50 % | Nominal Strain; 50 mm/min |
| Elongation at Yield | 9.0 % | 9.0 % | 50 mm/min |
| Tensile Modulus | 0.600 GPa | 87.0 ksi | 1 mm/min |
| Tensile Creep Modulus, 1 hour | 520 MPa | 75400 psi | |
| Tensile Creep Modulus, 1000 hours | 350 MPa | 50800 psi |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 170 µm/m-°C @Temperature 20.0 °C |
94.4 µin/in-°F @Temperature 68.0 °F |
|
| CTE, linear, Transverse to Flow | 177 µm/m-°C @Temperature 20.0 °C |
98.3 µin/in-°F @Temperature 68.0 °F |
|
| Melting Point | 220 °C | 428 °F | 10°C/min |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 7.80e+13 ohm-cm | 7.80e+13 ohm-cm | |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | |
| Dielectric Constant | 3.7 @Frequency 1e+6 Hz |
3.7 @Frequency 1e+6 Hz |
|
| 4.1 @Frequency 100 Hz |
4.1 @Frequency 100 Hz |
||
| Dielectric Strength | 34.0 kV/mm | 864 kV/in | |
| Dissipation Factor | 0.050 @Frequency 1e+6 Hz |
0.050 @Frequency 1e+6 Hz |
|
| 0.13 @Frequency 100 Hz |
0.13 @Frequency 100 Hz |
||
| Comparative Tracking Index | 600 V | 600 V |